Influence of Acid Frosting on the Microstructure Characteristics and Mechanical Strength of Eroded Soda-Lime-Silica Glasses by Sandstorm
Journal Title: International Journal of Structural Glass and Advanced Materials Research - Year 2017, Vol 1, Issue 1
Abstract
Most glass products such as cars windshields, solar panels protecting glass and windowpanes are exposed to unavoidable sandblasting effects especially in areas prone to sandstorms. This sand impingement results into micro cracks and surface flaws which altered the structure and strength of the exposed glasses thereby lowering their service life. In this regard, attempt was made in this research to investigate the influence of acid frosting technique as a means of surface modification on the microstructure characteristics and mechanical strength of eroded soda-lime-silica glass. Several glass samples measuring 80x60 mm were initially prepared and exposed to sand impingement from a sandblasting machine with an air flow speed of 15m/s and an impact angle of 90°. The sandblasted glass samples (Scontrol) were later immersed in Hydrofluoric Acid (HF) for acid frosting procedure at dipping period of 5, 10, 15 and 20 minutes respectively. Microstructure characteristics were examined using scanning electron microscopy while flexural strength test was conducted to assess the mechanical strength of the sample glasses. The results showed that mechanical strength of the etched-sandblasted samples (S+E series) improve significantly as the dipping period increases compared with sandblasted glasses. In term of microstructure, homogenously distributed micro-cracks and numerous flaws were observed on the eroded glass samples while for the S+E series, the stress riser effect of these micro-cracks are well eliminated which accounts for the strength improvement.
Authors and Affiliations
Akinwumi Gbenga Owoyemi, Grace Olufunke Matthew and Seun Samuel Owoeye
Keywords
Related Articles
- EP ID EP40349
- DOI -
- Views 322
- Downloads 0
Nonlinear Analysis of RC Box Culverts Resting on a Linear Elastic Soil
In the analyses presented, the soil-structure interaction is accounted for by means of a FE-BIE approach, in which the structure is modelled with displacement-based beam finite elements, whereas the boundary between stru...
Performance of Standard Statistical Distributions for Modeling Glass Fracture
Experimental data on the strength of new annealed float glass tested in an ambient environment was collected. A comparison was made between four standard distributions, the normal, lognormal, Gumbel and Weibull, with res...
Vulnerability and Protection of Glass Windows and Facades under Blast: Experiments, Methods and Current Trends
Glass has been overwhelmingly used for windows and facades for modern constructions. Nevertheless, due to its relatively low tensile strength and mostly brittle behaviour, compared to other structural members, glass wind...
Studies on Environmental Impact Assessment of Reinforced Concrete in Different Life Cycle Phases
Concrete is one of most used materials in construction and also one of the main responsible for the emission of carbon dioxide, or CO2, in the atmosphere. Thus, in order to study ways to reduce this impact, it is importa...
New Golden Red Sodium Calcium Silicate Glasses
Traditional golden red glasses were based on K2O-PbO-SiO2 composition system. In this paper, we reported new golden red glasses based on Na2O-CaO-SiO2 system without SnO2 and PbO in them. By using a spectrophotometer and...