The role of 1-hexene comonomer content in thermal behavior of medium density polyethylene (MDPE) synthesized using Phillips catalyst
Journal Title: Polyolefins Journal - Year 2014, Vol 1, Issue 2
Abstract
In this work, the role of comonomer content of 1-hexene-medium density polyethylene (MDPE) copolymer, synthesized using Phillips catalyst, on thermal behavior parameters such as: crystallization, melting temperature and thermal degradation was investigated in detail. The copolymer was fractionated to homogenous short-chain branching (SCB) fractions by "preparative temperature rising elution fractionation" (P-TREF) method and then it was subjected to thermal analyses. A broad chemical composition distribution (CCD) in terms of SCB content and molecular weight (Mw) was observed by P-TREF and gel permeation chromatography (GPC), respectively. Based on P-TREF results, a parabolic relationship between methylene sequence length (MSL) and elution temperature (ET) was presented. Differential scanning calorimetry (DSC) showed distinct, well-defined melting peaks over a 22 °C temperature range for SCB contents of about 3-12 (br/1000 C). The variations in physical characteristics such as melting temperature (Tm), crystallinity (Xc), crystallization temperature (Tc) and lamellae thickness (Lc) against SCB content were correlated. Thermogravimetric analysis (TGA) suggested linear relationships between the temperature at maximum degradation rate (Tmax) as well as the degradation initiation temperature (T5%) versus SCB content. Moreover, the TGA curves exhibited distinct differences at both initiation and propagation stages of thermal degradation at dissimilar comonomer contents.
Authors and Affiliations
Abbas Kebritchi, Mehdi Nekoomanesh, Fereidoon Mohammadi, Hossein-Ali Khonakdar
Keywords
Related Articles
- EP ID EP283076
- DOI 10.22063/POJ.2014.1099
- Views 119
- Downloads 0
Dissymmetric dinuclear transition metal complexes as dual site catalysts for the polymerization of ethylene
A series of dissymmetric dinuclear complexes were synthesized, as dual site catalysts in ethylene polymerization, by coupling the allylated a-diimine complexes of the metals Ti, Zr, V, Ni and Pd with the ansa-zirconocene...
High porosity polyethylene aerogels
Monolithic aerogels of high molecular weight polyethylene (Mw= 3x106- 6x106 g/mol) have been prepared by solvent extraction with supercritical carbon dioxide from thermoreversible gels prepared in decalin. These low dens...
Oxygen-barrier films based on low-density polyethylene/ ethylene vinyl alcohol/ polyethylene-grafted maleic anhydride compatibilizer
In this research, high oxygen-barrier films were organized based on low-density polyethylene (LDPE)/ ethylene vinyl alcohol (EVOH)/ polyethylene-grafted maleic anhydride (LDPE-g-MA) compatibilizer. The effects of 10–30 w...
Testing DFT ability to predict the stereoselectivity of group 4 metallocenes in propylene polymerization
In this study we have tested the ability of a standard DFT computational protocol to reproduce the experimentally obtained stereoselectivity of 26 different C2-symmetric zirconocene catalysts active in propylene polymeri...
Polymerization of propylene in a minireactor: Effect of polymerization conditions on particle morphology
Gas phase polymerization of propylene was carried out in a semi-batch minireactor using a commercially supported Ziegler–Natta (ZN) catalyst. The influence of variables including monomer partial pressure, external electr...