A study of electrochromiс Ni(OH)2 films obtained in the presence of small amounts of aluminum

Abstract

<p class="1">The research is related to the synthesis of electrochromic films of nickel hydroxide with aluminum as a dopant. Films were deposited via cathodic template synthesis in the presence of polyvinyl alcohol from solutions containing 0.01 M Ni(NO<sub>3</sub>)<sub>2</sub> and Al(NO<sub>3</sub>)<sub>3</sub>. Aluminum nitrate was added in different concentrations: 0.138, 0.257 and 0.550 mM. The necessary aluminum concentration was calculated based on the theoretical grounding with the use of Faraday’s law equation. All of the prepared films demonstrated electrochemical activity, and the film deposited from the solution containing 0.01 M Ni(NO<sub>3</sub>)<sub>2</sub> and 0.138 mM Al(NO<sub>3</sub>)<sub>3</sub> has demonstrated the best results. The film cycled reversibly with the coloration degree of – 81 %. At the same time, the film prepared under the same conditions without the dopant demonstrated the coloration degree of 75.8 %.</p><p class="1">All films deposited in the presence of aluminum had lower switching, especially bleaching, speed in comparison to the undoped reference sample.</p><p class="1">Morphology study of the prepared films revealed that the latter differs little. The film deposited in the presence of 0.138 mM Al(NO<sub>3</sub>)<sub>3</sub> had spherical formations on its surface. It was also found that the morphology of the substrate, which was glass coated with SnO<sub>2</sub>:F, differed significantly from the morphology of the films deposited with and without the dopant.</p><p class="1">The film deposited from the solution of 0.01 M Ni(NO<sub>3</sub>)<sub>2</sub> and 0.138 мМ Al(NO<sub>3</sub>)<sub>3</sub> was confirmed to contain aluminum. The mass ratio of aluminum to nickel in the Ni–Al-138 film varied between 1:10.23 and 1:6.44.</p>

Authors and Affiliations

Valerii Kotok, Vadym Kovalenko

Keywords

Related Articles

Activation of the nickel foam as a current collector for application in supercapacitors

<p>Nickel foam is widely used as a current collector and as a major component of the faradic electrode in supercapacitors. Activation of nickel foam would allow increasing the capacity of the nickel hydroxide electrode o...

Development of an intelligent decision support system to control the process of well drilling under complicated conditions

<p>The paper addresses the task on constructing a method for the identification of complications, arising during oil and gas well drilling, which functions under conditions of an a priori and current uncertainty under th...

Research into the structural-mechanical properties of shortbread dough with oilseed meals

<p>This paper reports results of research into the application of oil-seed meal in the technology of flour-based confectionery products, specifically shortbread dough. We have investigated the structural-mechanical prope...

Study of the mathematical models of optimal partitioning for particular cases

<p>The basic problem of optimal sets partitioning (OSP) for the case, where a segment of a plane curve is a set, was stated. The problem is stated as follows: let us assume there is a segment of a plane curve, it is requ...

Development of a method for predicting the recurrence of states of atmospheric air pollution concentration in industrial cities

This paper reports the method developed for predicting the recurrence of states related to air pollution at industrial cities based on the modified window measure. The new scientific result implies that dangerous states...

Download PDF file
  • EP ID EP666637
  • DOI 10.15587/1729-4061.2019.168863
  • Views 56
  • Downloads 0

How To Cite

Valerii Kotok, Vadym Kovalenko (2019). A study of electrochromiс Ni(OH)2 films obtained in the presence of small amounts of aluminum. Восточно-Европейский журнал передовых технологий, 3(12), 39-45. https://europub.co.uk/articles/-A-666637