Accelerated Corrosion Fatigue Crack Growth Studies On Is 2062 Gr. E 300 Steel

Abstract

Corrosion fatigue crack growth experiments were carried out on two Eccentrically-Loaded Single Edge notch Tension [ESE(T)] specimens made of IS 2062 steel in salt water environment. The tests were carried out using ±250 kN capacity servo controlled electro hydraulic fatigue rated Universal Testing Machine (UTM). The test location of the specimen was placed in a chamber containing 3.5% Sodium Chloride (NaCl) aqueous solution which acted as corrosive environment. The corrosion process was accelerated by passing a constant direct current of 0.1 A and 0.3 A using an external current source. The maximum and minimum load values were 15 kN and 1.5 kN. The test frequency was 0.375 Hz and stress ratio was 0.1. Crack growth was continuously monitored and crack growth curve was plotted. From this curve, the fatigue crack growth constants C and m were determined. Details of the experimental study and the results are presented in this paper.

Authors and Affiliations

S. Menaka, G. Raghava, S. Vishnuvardhan, D. Suji

Keywords

Related Articles

Study on the Effect of Elevated Temperatures on Residual Compressive Strength of Ternary Blended Concrete using Fly Ash and Micro Silica

Reduction of carbon dioxide emission in to environment has become major challenge to the present scientists. One ton of cement consumption produces one ton of carbon dioxide which damage the climate. Replacement of ceme...

Study of Process Parameters Used in Wireelectric Discharge Machining

Wire electric discharge machining (Wire-EDM) is one of the widely accepted advanced machining processes used to machine components with intricate shapes and profiles.The wire is slowly fed through the material and the e...

A Review of Water Absorption, Porosity and Sorptivity of Cement Mortar made with metakaolin and flyash partially replaced in cement cured in seawater

In this present study the effects of flyash, metakaolin and their combinations has been evaluated for optimal level of replacement as blending component in cement. The results showed that the water absorption, porosity...

LTE Techniques in 4G Wireless System Using Protocol Stack

LTE, an acronym for Long-Term Evolution. 4G LTE is a standard for wireless broadband technology designed to support roaming Internet access via cell phones and handheld devices. Due to the requirements on high data rate...

Performance investigation of axial flow compressor at different climatic conditions

This paper discusses the effect on axial-flow compressor, when climatic conditions are changing. Ensuring compressor run at maximum effectiveness is a primary aim for operators. In the existing economic climate, whateve...

Download PDF file
  • EP ID EP22097
  • DOI -
  • Views 188
  • Downloads 4

How To Cite

S. Menaka, G. Raghava, S. Vishnuvardhan, D. Suji (2016). Accelerated Corrosion Fatigue Crack Growth Studies On Is 2062 Gr. E 300 Steel. International Journal for Research in Applied Science and Engineering Technology (IJRASET), 4(5), -. https://europub.co.uk/articles/-A-22097