Bond strength of resin cements to leucitereinforced ceramics
Journal Title: RSBO - Year 2012, Vol 9, Issue 2
Abstract
Objective: The aim of this study was to evaluate the shear bond strength (SBS) of two resin cements to four leucite-reinforced ceramics. Material and methods: Forty ceramic blocks (4 mm wide, 14 mm length and 2 mm thick) were used and the samples abraded with aluminum oxide (90 µm). The samples were divided into eight groups (n = 5). Two resin cements (conventional RelyX ARC and self-adhesive RelyX U100 – 3M ESPE) were bonded to Creapress (CRE-Creation/Klema), Finesse All-Ceramic (FIN-Dentsply/ Ceramco), IPS Empress Esthetic (IEE-Ivoclar Vivadent) and Vita PM9 (PM9- Vita). For all groups and in each ceramic block, after application of 10% hydrofluoric acid and silanation, three Tygon tubings were positioned over the ceramics, which were filled in with the resin cements (light-cure for 40 s). The tubings were removed to expose the specimens in format of cylinders (area: 0.38 mm2 ) and samples were stored in relative humidity at 24±2 °C for one week. After this period, each sample was attached to testing machine and the specimens were submitted to shear bond test (applied at the base of the specimen/cement cylinder with a thin wire/0.2 mm) at speed of 0.5 mm/ min, until failure. The results were analyzed by two-way ANOVA (resin cements and ceramic systems) and Tukey test (p<0.05). Results: The means (SD) were (in MPa): ARC + CRE = 32.1±4.3; ARC + FIN = 28.3±3.7; ARC + IEE = 25.9±4.4; ARC + PM9 = 22.2±2.1; U100 + CRE = 38.0±5.2; U100 + FIN = 36.9±2.8; U100 + IEE = 38.4±2.9; U100 + PM9 = 34.3 ±7.3. U100 showed higher SBS to ceramics than ARC. U100 had higher SBS when applied on IEE ceramic than on PM9. For ARC, SBS obtained with CRE was higher than with IEE and PM9. Conclusion: RelyX U100 can provide higher SBS to leucite-reinforced ceramics than conventional resin cement. The resin cements applied on the PM9 ceramic surface resulted in lower SBS.
Authors and Affiliations
Rubens Garcia, Reinaldo do Nascimento, Ana Cristina Gomes, Marcelo Giannini, Luiz Miguel, Peter Moon
Keywords
Related Articles
- EP ID EP125009
- DOI -
- Views 147
- Downloads 0
Fibromyalgia and temporomandibular dysfunction: a literature review
Introduction and objective: Several studies have associated temporomandibular disorders (TMD) and fibromyalgia (FM) finding a wide variation of results. The aim of this study was to review the literature about the relati...
Intentional replantation: case report of an alternative treatment for endodontic therapy failure
The aim of this study was to present an alternative treatment after the occurrence of endodontic therapy failure. The authors report a clinical case of a second maxillary permanent molar, which was indicated for intentio...
A Influência de Diferentes Métodos de Obtenção NA Ampliação do comprimento cervical de Trabalho em Primeiros testes Canais mésio-vestibular do molar superior
A ampliação dos canais radiculares utilizando diferentes tipos de métodos e instrumentos é o foco de inúmeras pesquisas na área de Deontologia. O objetivo deste estudo foi determinar a influência de quatro sistemas disti...
Evaluation of active chlorine releasing of sodium hypochlorite during seven days, stored at different temperatures
Introduction: The sanitation of the canal system through irrigation/aspiration, at the changing of the endodontic instruments aims to the excised material, removal of microorganisms and the cleaning of the walls of...
Definir tempos de mais óxido de zinco e eugenol com base cimentos endodônticos
Objective: To analyse ex-vivo setting times of national zinc oxide and eugenol based root canal sealers: Endofill®, Intrafill®, Rickert’s sealer (LenzaFarm®), Pulp Fill® and Target®. Material and methods: The setting tim...