EFFECT OF AUSTENITISING ON THE STRUCTURE AND PROPERTIES OF LOW-ALLOY Cr-Mo-V STEELS AFTER LONG-TERM OPERATION IN CREEP CONDITIONS FOR THE POWER INDUSTRY
Journal Title: Prace Instytutu Metalurgii Żelaza - Year 2018, Vol 70, Issue 2
Abstract
The article concerns the revitalising heat treatment of components of the pressure part of power units operating under creep conditions. The possibilities of “recovering” the structure and functional properties similar to those of the initial state are shown on the example of elbows and straight sections made of 14MoV6-3 steel (13HMF), after long-term opera-tion, significantly beyond the computational working time, with slightly diversified but significant exhaustion. It is possible by selecting the type and parameters of heat treatment depending on the structure class after operation and the corresponding degree of exhaustion. The effectiveness of revitalising heat treatment is shown, especially in relation to the recovery of impact resistance and creep resistance due to the obtained structure corresponding to the initial state. The defined limitation in the operation of revitalising heat treatment of materials after long-term operation in creep conditions is the structure after operation, in which the initiation of internal damages as a result of creep will be revealed.
Authors and Affiliations
Tadeusz Jóźwik
Keywords
Related Articles
- EP ID EP429663
- DOI 10.32730/imz.0137-9941.18.2.01
- Views 69
- Downloads 0
RESIDUAL LIFE OF REPAIR WELDED JOINTS IN PIPELINES MADE OF 13HMF AFTER USE FOR THE DESIGN OPERATING TIME
This paper presents the results of material tests of repair welded joints carried out for samples of materials taken from high pressure steam pipelines after over 200,000 operating hours in creep conditions, made of the...
Forecasting the development of the national construction market in terms of the economic crisis
The paper considers the main problems in the construction market in Ukraine economic crisis and analyzes the structural problems of the industry, studied the experience of transformation construction industries in oth...
MICROSTRUCTURE AND MECHANICAL PROPERTIES OF A SIMILAR T24 STEEL WELDED JOINT AFTER SERVICE
The material under investigation was a welded joint made of 7CrMoVTiB10-10 (T24) steel after 36,000 hours of use at the temperature of 540°C and pressure of 27 MPa. The test samples for the study were taken from a membra...
WPŁYW WYKORZYSTANIA RUD ŻELAZA O PODWYŻSZONEJ ZAWARTOŚCI CHLORU NA PROCES SPIEKANIA
W artykule przedstawiono ocenę możliwości wykorzystania rud żelaza o podwyższonej zawartości chloru w procesie spiekania. Przeprowadzono laboratoryjne próby spiekania ze zwiększonym udziałem rudy żelaza o podwyższonej za...
INFLUENCE OF HAFNIUM ON HIGH TEMPERATURE OXIDATION OF NiAl AND Ni3Al ALLOYS
The results presented in this paper concern the modification of NiAl and Ni3Al alloys with reactive elements that in-crease their high temperature oxidation resistance. Literature data indicate that even trace additions...