EFFECT OF SHOT PEENING ON FATIGUE PROPERTIES OF STEEL IN DIFFERENT STRUCTURAL STATES
Journal Title: Materials Engineering - Materialove inzinierstvo (MEMI) - Year 2011, Vol 18, Issue 2
Abstract
The aim of this paper is to evaluate the effect of shot peening on fatigue properties of dual-phase steels DP 600 in received condition, as well as in condition after different regimes of heat treatment. In the work, there are presented results of tests on smooth samples as well as on samples with stress concentrator (a drilling hole, size d = 4mm). The expectations, that shot peening of flat steel samples improves resistance to fatigue failure, were approved by all tested structural states. The tests on samples with the drilled hole showed, that effect of shot peening on fatigue properties may be negative, if the hole was drilled after shot peening of surface of samples.
Authors and Affiliations
Gejza Rosenberg
Keywords
Related Articles
- EP ID EP102914
- DOI -
- Views 116
- Downloads 0
Study of the influence of agricultural waste on the porosity of clay brick
This paper deals with the influence of two organic residues on the porosity of clay bricks. The insulation capacity of the brick increases with increasing the porosity. Combustible organic additions are often used to for...
Corrostion resistance of the welded AISI 316L after various surface treatments
The main aim of this work is to monitor the surface treatment impact on the corrosion resistance of the welded stainless steel AISI 316L to local corrosion forms. The excellent corrosion resistance of austenitic st...
Experimental analysis of influence of different lubricants types on the multi-phase ironing process
This paper is aimed at presenting results of an experimental analysis of the different types of lubricants influence on the multi-phase ironing process. Based on sliding of the metal strip between the two contact element...
INFLUENCE OF SHOT PEENING ON AISI 316Ti FATIGUE PROPERTIES
This paper deals with examination of fatigue properties of AISI 316Ti stainless steel before and after shot peening including analysis of residual stress relaxation during rotating bending fatigue tests (f = 50 Hz, T = 2...
MICROSTRUCTURE AND MECHANICAL PROPERTIES DEGRADATION OF CrMo CREEP RESISTANT STEEL OPERATING UNDER CREEP CONDITIONS
In this contribution microstructure degradation of a steam tube is analysed. The tube is made of CrMo creep resistant steel and was in service under creep conditions at temperature 530°C and calculated stress level in th...