Еlectrophysical properties of carbon nanotubes/NiCo composites
Journal Title: Хімія, фізика та технологія поверхні - Year 2018, Vol 9, Issue 4
Abstract
Metal-containing nanocomposites containing nanoparticles of organic and inorganic materials, attract considerable attention of specialists in recent years due to a large number of possible applications. NiCo nanoparticles have been obtained on the surface of unoxidized and oxidized multiwall carbon nanotubes (MWCNT) by chemical precipitation of the corresponding carbonates from a solution of hydrazine hydrate at a temperature of 350 K. Oxidation of MWCNT was carried out in a solution of ammonium bifluoride and sulfuric acid. The purpose of this work is to synthesize composites of MWCNT/NiCo and to find differences in their electrophysical properties dependent on the nature of the MWCNT surface. The transmission electron microscopic and radiographic studies showed the presence of phases composites with the size of crystallites of 20–30 nm. The packing density of agglomerates of metal particles is higher in composites with unoxidized MWCNT. The metal particles are arranged on the surface of MWCNT more evenly and in shape more close to spherical in composites with oxidized MWCNT. The method of thermogravimetric analysis shows that the process of composites oxidation during heating for a composite containing oxidized MWCNT is more intense. It indicates a smaller particle size of metals. The real and imaginary components of the complex dielectric and magnetic permeabilities of the disperse composites was determined by the methods of ultrahigh-frequency interferometry. The corresponding values are somewhat higher for composites containing oxidized MWCNT in the ultrahigh-frequency range. The values of imaginary magnetic permeability are higher by 18 % for unoxidized MWCNT composites at low frequencies. The electrical conductivity at low frequencies is 2.9 and 1.6 Ohm–1·cm–1 for composites containing unoxidized and oxidized MWCNTs, respectively.
Authors and Affiliations
O. M. Lisova, S. M. Makhno, G. M. Gunya, P. P. Gorbyk
Keywords
Related Articles
- EP ID EP462725
- DOI 10.15407/hftp09.04.362
- Views 75
- Downloads 0
Синтез багатошарового азаграфена та оксиду нітриду вуглецю
Графітоподібний нітрид вуглецю (що характеризується як нетоксичний і хімічно високостійкий матеріал) і його наноструктуровані і доповані, зокрема, киснем, похідні, привертають особливу увагу в якості найбільш перспективн...
Properties of polyethylene–carbon nanotubes composites
The production of stable dispersions of carbon nanotubes (CNTs), synthesized by CVD, in different liquids, is one of the methods of preparation of CNTs for introduction into polymeric matrix. The aim of this work is to p...
Light emitting “polymer-nanoparticles” coatings on macroporous silicon substrates
We investigate the conditions for increase of the photoluminescence of CdS nanocrystals in polyethyleneimine and polyethyleneimine with carbon multiwall nanotubes on macroporous silicon substrates. Macroporous silicon st...
Релаксація розподілу надлишкових неосновних носіїв заряду в макропористому кремнію
Релаксація розподілу надлишкових неосновних носіїв заряду в структурі макропористого кремнію була розрахована методом кінцевих різниць. Початковий розподіл надлишкових неосновних носіїв заряду має два максимуми, після ге...
Вплив будови полімерної матриці на кінетичні та термомеханічні властивості органо-неорганічних композитів на основі ТЕОС
Досліджено вплив будови полімерної матриці гібридних органо-неорганічних композитів на основі системи моно- або диметакрилату та тетраетоксисилану, а також їх складу на термомеханічні властивості і молекулярну структуру...