EXTRACTION OF THE VALUABLE COMPONENTS FROM NON-FERROUS METALS-CONTAINING POOR ORE AND TAILINGS
Journal Title: Azerbaijan Chemical Journal - Year 2018, Vol 0, Issue 1
Abstract
In the article the results of processing oxidized copper polymetal ore and iron ore tailings by heap leaching irrigation and sorption methods have been analyzed. A study was made of conditions for concentrating some non-ferrous metals (Cu, Zn, Ag, Au, Co, Mn) by hydrolytic precipitation and sorption methods. As well, it is reported on the results, were obtained, on utilization of arsenic from technological solutions to the demand level of concentration
Authors and Affiliations
A. A. Haydarov, A. B. Muradova, A. N. Aghayev
Keywords
Related Articles
- EP ID EP470405
- DOI 10.32737/0005-2531-2018-1-104-110
- Views 102
- Downloads 0
CONTROL OF THE PROCESS OF THE DEHYDROGENATION OF ETHYLBENZENE IN STYRENE, FLOWING UNDER NONSTATIONARY CONDITIONS
A new method, different from the industrial one is suggested, for carrying out the process of dehydrogenation of ethylbenzene in styrene, consisting in gradual lowering of the temperature of the raw material at the inlet...
COMBINATION OF THE TECHNOLOGICAL REJIME OF PYROLYSIS AND THE QUALITY OF HEAVY RESIN
The dependence the yield and content of heavy resin of pyrolysis on the initial raw material of hydrocarbon has been investigated. It is shown noted that at approaching by-products which contain very valuable hydrocarbon...
ALKYLATION OF ETHYLBENZENE BY ETHANOLE ON H-ULTRASIL ZEOLITE CATALYST, MODIFIED BY LANTANUM
The modified H-ultrasil zeolite maintained high crystallinity and high specific surface areas precursors testified by XRD, BET and NH3-TPD analysis. Effect of lanthanum concentration on the adsorptive, acidic and catalyt...
GRAPHITE INTERCALATED COMPOUND
The article highlights the synthesis of graphite intercalated compound (PCl3-GIC) via the chlorophosphorylation process. PCl3 was used as intercalate for the synthesis of PCl3-GIC and the excess of PCl3 was removed by wa...
PHASE RELATIONS IN THE Cu8GeS6–Ag8GeS6 SYSTEM AND SOME PROPERTIES OF SOLID SOLUTIONS
Phase equilibria in the Cu8GeS6–Ag8GeS6 system were experimentally investigated by means of differential thermal analysis, powder X-ray diffraction techniques, and electromotive force (EMF) measurements of concentration...