Influence of CuxTe back contact on CdS/CdTe photovoltaic device
Journal Title: Science Paper Online - Year 2009, Vol 4, Issue 4
Abstract
CuxTe polycrystalline thin films were prepared by co-evaporation method. The influence of the film characteristic on the CdS/CdTe photovoltaic device performance was investigated by XRD. The results show that as deposited CuxTe thin films were amorphous phase. While after annealing, samples were polycrystalline phases with increasing temperature. Especially, when NCu∶NTe was 1∶1.44 the film showed more evident polycrystalline phase and the crystallization degree increased. When the main CuTe phase structure was used as the back contact layer of CdTe solar cells, the characteristic of the device did not be improved and conversion efficiency (η) decreased. On the contrary, when the main Cu1.44Te phase structure was used as the back contact layer, η increased. Especially, when the thickness of the film was 40 nm, η was the biggest. Compared with the back contact layer of Cu1.44Te phase structure，the back contact layer of Cu2Te phase structure made the characteristic of CdTe solar cells decreased a little, but better than that without back contact layer.
Authors and Affiliations
Huijin Song, Jiagui Zheng, Lianghuan Feng
Keywords
Related Articles
- EP ID EP96848
- DOI -
- Views 108
- Downloads 0
围压对水射流动力学特性影响的实验研究
围压是影响射流动力学特性的重要参数之一。运用自行研制的高压釜装置实验研究了围压对射流冲击压力、空化噪声与脉冲特性及冲蚀破岩效率的影响规律，分析了围压对射流冲蚀破岩能力的影响机制，最高射流驱动压力40 MPa、围压20 MPa。结果表...
固定化微生物处理高氨氮废水的影响因素研究
本文以人工配制的无机高氨氮废水为处理对象，利用以大孔聚氨酯载体为填料的固定化微生物曝气生物滤池为反应器，研究DO、pH、水力停留时间(HRT)和进水氨氮浓度对反应系统硝化性能的影响，以确定该系统的最佳操作条件。结果表明：进水氨氮...
添加CaCO3对煤灰熔融性影响及其机理的研究
考察了CaCO3不同添加量对三种低灰熔点煤样的软化温度(ST)的影响，揭示了CaCO3对煤灰熔融性的影响规律。同时结合X射线衍射技术及CaO—Al2O3—SiO2 三元相图探讨了加入CaCO3后的煤灰熔融机理。结果表明，煤灰熔点随CaCO3加入量的提高先降后升...
Study on composite lignosulphonate-based slurry water-reducer
A new type water-reducer for raw cement slurry was developed, which consists of mostly calcium lignosulphonate and a little modified agent N. When adding this kind of composite water-reducer into raw cement slurry, the w...
A novel soluble polyamide-imide from new fluorinated diamine
[1,4-bis(4-amino-3-trifluoromethylphenoxy)benzene (B)], a new fluorinated diamine monomer were synthesized in this paper. PAI(C) is prepared from the diamine (B) and trimellitic anhydride chloride (TMAC) by one-step meth...