Influence of Nano-Diamond Particles on the Tribological Characteristics of Nickel Chemical Coatings
Journal Title: Tribology in Industry - Year 2014, Vol 36, Issue 2
Abstract
Friction and wear of 10 types Ni chemical coatings, with and without heat treatment, containing nano-diamond particles of various size – 0;5 nm; 100 nm; 200 nm and 250 nm, are studied in the paper. Procedure and laboratory device for friction investigation in starting regime were developed. Experimental results for the influence of the particle size on the static friction force and the change of friction coefficient have been obtained. Abrasive wear has been studied by means of the procedure developed by the authors for the study of above coatings under conditions of dry friction on surfaces with fixed abrasive. The obtained results are related to the parameters linear wear, wear rate and wear-resistance. A part of this study is connected with the tasks on the 7 FP Project „Acom In (Advanced Computing Innovations)” coordinated by the Institute of Information and Communication Technologies at the Bulgarian Academy of Sciences, and the other part is carried out under the Project ДУНК-01/3 “University R&D Complex for innovation and transfer of knowledge in micro/nano-technologies and materials, energy efficiency and virtual engineering” funded by the Bulgarian Ministry of Education and Science.
Authors and Affiliations
M. Kandeva , D. Karastoianov , B. Ivanova , V. Pojidaeva
Keywords
Related Articles
- EP ID EP147529
- DOI -
- Views 92
- Downloads 0
Development of Mobile Device for Oil Analysis
This paper presents the results of project focused on development and practical application of mobile instrument for on-site analysis of industrial oils. For years, the implementation of the oil analysis was limited to a...
Wear Behavior of Uncoated and Coated Tools under Complex Loading Conditions
In automotive industry crash relevant structures of the body in white are manufactured using the direct hot stamping process. Due to the high temperature difference between the hot blank and the cold tool surfaces and th...
Effect of Heat Treatment on Wear behavior of Hybrid Aluminum Metal Matrix Composites
The focus of the paper is the wear behavior of hybrid aluminum metal matrix composites. The main objective of the investigation is to conduct the wear test at room temperature for both the as-cast and age hardening condi...
Mo-C Multilayered CVD Coatings Mo-C Multilayered CVD Coatings
Production processes of multi-layered Mo-C coatings by the method of chemical vapor deposition (CVD) with the use of organometallic compounds were developed. Coatings are applied on technical purpose steel DIN 1.2379 (Х1...
Wear Performance Optimization of Electroless Ni-B Coating Using Taguchi Design of Experiments
The present study outlines the use of Taguchi parameter design to minimize the wear performance of electroless Ni-B coating by optimizing the tribological testing parameters. The tests are carried out in a multi- tribote...