INVESTIGATION OF MODIFIED WITH IONS OF HYDROGEN, PALLADIUM(II), AND COPPER(II) BY IR AND DIFFUSE REFLECTANCE SPECTRAL METHODS
Journal Title: Вісник Одеського національного університету. Хімія - Year 2016, Vol 21, Issue 2
Abstract
Changes appeared in IR and diffuse reflectance UV-vis spectra of clinoptilolite as a result of its modification by boiling in nitric acid solutions (0.25-3 M) and anchoring active components on it were analyzed. As was shown by IR spectroscopy, the increase in acid concentration caused a high-frequency shift of the band attributed to asymmetric stretching vibrations of the Si-O-Al fragment due to the clinoptilolite dealumination. The values of this shift were not changed after active components anchoring on the acid modified clinoptilolite samples. The band of deformation vibrations of OH groups in water molecules (at 1633 cm-1 for natural clinoptilolite) was weakly affected (a slight high-frequency shift) by the acid concentration increase and remained practically unaffected by anchoring palladium and copper ions. However, the effect of Pd(II) and Cu(II) anchoring on IR spectra could be observed through a low-frequency shift of the band characterizing stretching vibration νОН of OH groups in water molecules indicating some disturbance of hydrogen bonds in H2O molecules and a change in their energy. The UV region of diffuse reflectance UV-vis spectra of all anchored catalyst samples showed the appearance of new intense bands at 224-226, 279-284, and 327-334 nm which were absent Pd-Cu complexes which attendance is necessary for catalytic low-temperature oxidation of carbon monoxide with air oxygen. It should be noted that a new band appeared at 351-363 nm would be assigned to individual Pd(II) indicating that some portion of palladium(II) ions did not participate in the formation of the catalytically active bimetallic Pd-Cu complexes. The presence of individual palladium(II) was confirmed by the fact that only the bends characteristic of square planar palladium(II) complexes were observed in the palladium(II) absorbing region in the visible part of diffuse reflectance UV-vis spectra. Additionaly, theses spectra also contained the bends corresponding to d-d transition in the bimetallic palladium-copper complexes. As well, a low-intensity band centered at 740-750 nm could be assigned to copper situated in the bimetallic Pd-Cu complexes because the band was shifted towards the lowfrequency region as compared with the mononuclear octahedral aqua complex of copper(II). Judging from these diffuse reflectance UV-vis spectral data and the results obtained in our previous works, the optimal conditions for formation of the clinoptilolite anchored Pd-Cu complexes were achieved when clinoptilolite was boiled in 3 M HNO3 for 30 min.
Authors and Affiliations
T. L. Rakytskaya, K. O. Golubchik, Т. A. Kiose, A. A. Ennan, I. V. Stoyanova
Keywords
Related Articles
- EP ID EP337049
- DOI 10.18524/2304-0947.2016.2(58).74773
- Views 77
- Downloads 0
SPECTROSCOPIC STUDIES OF COMPLEX COMPOUNDS OF COBALT(III) -NICKEL(II) WITH DIETANOLAMINE
Polynuclear complex compounds of 3d metals with amino alcoholic ligands can be used to obtain effective electrocatalysts for the process of lithium intercalation in graphite from organic aprotic electrolytes, occurring i...
THE INTERACTION OF DIRHENIUM(III) CLUSTER COMPOUNDS WITH SUCCINIC ACID
Complex compounds of dirhenium(III) with bridge carboxylates and halide ligands show various types of bioactivity, and the entry into the internal coordination sphere of the central “atom”- complexing the ligands that ha...
ADSORPTION-DESORPTION PROPERTIES OF NATURAL AND MODIFIED TRIPOLI TOWARDS Cu(II) AND Pd(II) AS COMPONENTS OF CATALYSTS FOR CARBON MONOXIDE OXIDATION
Adsorption of copper(II) ions by natural tripoli and its modified forms obtained as a result of using different treatment methods for natural tripoli modification, i.e. thermal treatment in air, boiling in water, and boi...
INFLUENCE OF THERMAL TREATMENT ON THE PHYSICAL AND CHEMICAL PROPERTIES OF NANOCRYSTALLINE 88 ZrO2 - 12 CeO2 (MOLE %) POWDER
Transformation toughening, based on the martensitic T-ZrO2 → M-ZrO2 phase transformation, causes the high strength of ZrO2-based composites. The reversible martensitic phase transformation of fine-grained composites ZrO2...
INTERACTION OF THE LANTHANA, YTTRIA WITH YTTERBIA AT TEMPERATURE 1500 °C
Phase equilibria in the ternary La2О3–Y2O3–Yb2О3 system at 1500 °C were studied by X–ray diffraction and petrography in the overall concentration range. The samples of different compositions have been prepared from nitra...