Investigation of the initial degradation stage and tensile strength of polylactide and its composites with eggshells

Journal Title: Engineering of Biomaterials / Inżynieria Biomateriałów - Year 2018, Vol 21, Issue 146

Abstract

The degradation rate of the composite polylactide (PLA) – eggshell powder (ESP), depends on many factors. The main are porosity, particle distribution, the weight load of ESP and chain length, the microstructure of bio-based and biodegradable PLA polymer. Bio-additives introduced to polymer matrix may have an impact on mechanical properties of the composite. Natural bone structure inspires to design mimicry materials. Materials which combine inorganic and organic components are of highly complex structure. The paper focuses on the investigation of tensile strength and the initial stage of degradation of PLA and its composites with ESP in two media, i.e. H2O and PBS. ESP was obtained by grinding, stirring with mixture 14.5 wt.% NaOH and 85.5 wt.% ethanol, and drying. Samples containing: 0, 10 and 20 wt.% of ESP were prepared. Dumbbell-samples were made by injection molding, and their mechanical properties were measured. Tensile results suggest that Young’s modulus increased and tensile strength decreased as the amount of ESP is increased. Conductivity and pH of incubation media differed according to the material composition. SEM-EDS observations of PLA-ESP composites after fracture test were performed, and showed good adhesion between ESP and the polymer matrix. Influence of the incubation in H2O and PBS on PLA and PLA- -ESP composite surface degradation was checked. The PLA-ESP composites are characterized by a combination of unique properties, which may be suitable to use them as an eco-friendly packaging or medical material.

Authors and Affiliations

P. Szatkowski, K. Greń, M. Kisilewicz

Keywords

Related Articles

Operative treatment of bone fracture with Kirschner wires - young cat case

This case study shows a cross pin technique of treating an epiphyseal fracture using the Kirschner wires in the case of a ten-month old European cat. The radiological diagnosis was performed both before and after the imp...

Badanie własności fizykochemicznych bezcementowych panewek stawu biodrowego

Celem prowadzonych badań było porównanie własności panewki nowej oraz po alloplastyce rewizyjnej przebywającej w organizmie człowieka przez 68 miesięcy. W ramach badań przeprowadzono analizę składu chemicznego, własności...

In vitro biological evaluation of new dental biomaterials

Since the bactericidal effect of silver and gold is known, an attempt has been made to produce a new group of bactericidal biomaterials for use in restorative dentistry, containing nanoparticles of silver and gold. The a...

Wpływ dodatku kwasów karboksylowych na czas wiązania i wytrzymałość na ściskanie cementów szkło-jonomerowych

Cementy szkło-jonomerowe powstają w czasie utwardzania kompozycji złożonych z dwóch składników: szklanego proszku i płynu wiążącego będącego wodnym roztworem polikwasów alkenowych. Wiązanie cementu polega na reakcji kwas...

Modification of PLGA microspheres’ microstructure for application as cell carriers in modular tissue engineering

Microspheres (MS) made of resorbable polymer have been proposed as a cell growth support. They may be assembled to form cell constructs or be suspended in hydrogels allowing injection into injury location. High relative...

Download PDF file
  • EP ID EP553972
  • DOI -
  • Views 67
  • Downloads 0

How To Cite

P. Szatkowski, K. Greń, M. Kisilewicz (2018). Investigation of the initial degradation stage and tensile strength of polylactide and its composites with eggshells. Engineering of Biomaterials / Inżynieria Biomateriałów, 21(146), 18-23. https://europub.co.uk/articles/-A-553972