MECHANICAL AND TRIBOLOGICAL PROPERTIES OF OXIDE LAYERS OBTAINED ON Ti-6Al-7Nb ALLOY
Journal Title: Tribologia - Year 2016, Vol 267, Issue 3
Abstract
The research presented in the paper was focused on determining the effects of thermal oxidation parameters on the mechanical and tribological properties of oxide layers formed on Ti-6Al-7Nb titanium alloy for biomedical applications. Titanium alloy was oxidized at 600 and 700°C for 72h. The study found that, at lower temperatures, the oxidized alloy surface was covered by a nonuniform oxide layer. A 100°C increase in the treatment temperature yielded a uniform layer covering the whole surface of the alloy. Hardness measurements showed that thermal oxidation resulted in the formation of oxide layers characterized by a 3-fold higher hardness compared to untreated alloy. Tribological tests showed that thermal oxidation effectively improves the resistance of Ti-6Al-7Nb alloy to sliding wear. Tribological tests demonstrated that an increased oxidation temperature was associated with improved resistance to sliding wear.<br/><br/>
Authors and Affiliations
Krzysztof ANIOŁEK, Adrian BARYLSKI, Marian KUPKA, Michał DWORAK
Współczynnik restytucji prędkości cząstek podczas zderzenia z łopatkami młyna wirnikowego
WŁAŚCIWOŚCI TRIBOLOGICZNE ŚREDNIOWĘGLOWEJ STALI PO AZOTOWANIU POŁĄCZONYM Z NASTĘPNYM UTLENIANIEM I IMPREGNACJĄ
W pracy omówiono wyniki badań właściwości tribologicznych i korozyjnych warstw wytwarzanych na powierzchni stali średniowęglowej C45 w procesie azotowania gazowego połączonym z następną obróbką – utlenianiem i impregnacj...
ASSESSMENT AND ANALYSIS OF IMPREGNATED TRIBOLOGICAL SYSTEMS WORKING AT ELEVATED TEMPERATURES
With emphasis on the reduction of frictional resistance and tribological wear of machine component parts, it becomes more and more important, in order to improve their efficiency, durability and reliability. Friction cau...
The effect of zinc dithiophosphates on the friction and wear of partially stabilized zirconia. Part I. Zinc DI-N-alkyldithiophosphates tribological properties
Tribological properties of zinc di-n-alkyldithiophosphates (ZDTPs) of ionic-ZrO2, partially stabilised by Y2O3 (PSZ), were performed using a ball-disk tribometer, at 25°C. It was found that ZDTPs significantly reduce the...
THE TRIBOLOGICAL PROPERTIES OF NEW Ni-BASED TOOL MATERIALS
In the paper, the new Ni-based materials with a high carbon content, strengthened by intermetallic compounds, were presented. The chemical compositions of the new materials were designed in such a way as to obtain the ma...