Microstructure Analysis of Genuine Copper Alloy Coin
Journal Title: International Journal of Metallurgical & Materials Science and Engineering (IJMMSE) - Year 2018, Vol 8, Issue 1
Abstract
Coin characterization analysis (coins) is done by using the test method such as; Spectrometer XRF, XRD Defractometer, Deferential Scanning Calorimeter, Scanning Electron Microscope (SEM). Characterization is done in Lab Material Sciences Salemba UI to reveal the nature of coin properties related to mass density, coin base material, particle size of material, heat capacity properties. Qualitatively coins must have public security factors without having to reduce the function and security of the coin itself. The function of characterization testing is to see the superiority of coin material as a means of exchange of trade transactions, so that the coin is resistant to impact of scratches, resistant to corrosion when stored in the long term. In the physical configuration test, the coin dimension (diameter 27mm, 2mm thick) average coin mass of 7.48 gram / cc. The microstructure test with XRF element in coins is Cu, Ni, Al, P, Mn, Si. XRD test coin is an alloy Cu0.9Ni0.1 degan ring aluminum oxide. AlxOy Hardness CuNi 84.56 HV alloys, and AlxOy 72.55HV SEM test brass alloys show more than 2 kinds of micro grain figure material with almost the same grain size, while the aluminum compound has a grain figure of more than 2 kinds with different sizes.
Authors and Affiliations
EDIE SASITO SARWODIDOYO
Keywords
Related Articles
- EP ID EP281625
- DOI 10.24247/ijmmsefeb20181
- Views 129
- Downloads 0
Effect of Heat Treatment on Al2024 Reinforcement With Multiwalled Carbon Nanotube
In this research paper, Multiwalled carbon nanotubes (MWCNTs) reinforced with Al2024 were ball milled for homogenization of powder. Nanocomposite was developed using MWCNT reinforcement having 0.5%, 1.5%, and 2.5% weight...
FACTORS AFFECTING THE FORMATION OF GAS POROSITY IN A356 ALLOY WHEEL BY GRAVITY DIE CASTING
The majority of the defects occur in the in Aluminium alloy casting are due to mold parameters, filling and during solidification. Aluminium alloys form oxide layer on top of the molten metal in holding furnace immediate...
Dependence Parameters on Dielectric Behavior of Mo6+ Substituted Lithium Ferrites
High variance Mo6+ substituted lithium ferrite with general formula [Li (1+3y)/2MoyFe2.5-5y/2] O4: where y=0.05 to 0.5 in steps of 0.05 were prepared under solid- state reaction method sintered at high temperature 1200o...
EFFECT OF ECCENTRICITY PIN GEOMETRY ON THE FABRICATION OF SURFACE COMPOSITE (AL6061-T6 /SIC) BY FRICTION STIR PROCESSING
This research investigates the effect of three types of friction stir processing (FSP) tool with a pin eccentricity of 0, 0.5 and 1mm on the fabrication of AA6061-T6/SiC surface composites (SCs). The pin eccentricity ind...
Study on Reduction Kinetics of Iron Ore Sinter Using Coke Dust
Sintering is the most important process where iron ore fines are converted into a suitable lumpy product for blast furnace consumption. In this study, received sinter from Vizag Steel Plant, India has been used. The soli...