2D mapping of plane stress crack-tip fields following an overload

Journal Title: Frattura ed Integrità Strutturale - Year 2015, Vol 9, Issue 33

Abstract

 The evolution of crack-tip strain fields in a thin (plane stress) compact tension sample following an overload (OL) event has been studied using two different experimental techniques. Surface behaviour has been characterised by Digital Image Correlation (DIC), while the bulk behaviour has been characterised by means of synchrotron X-ray diffraction (XRD). The combination of both surface and bulk information allowed us to visualise the through-thickness evolution of the strain fields before the OL event, during the overload event, just after OL and at various stages after it. Unlike previous work, complete 2D maps of strains around the crack-tip were acquired at 60m spatial resolution by XRD. The DIC shows less crack opening after overload and the XRD a lower crack-tip peak stress after OL until the crack has grown past the compressive crack-tip residual stress introduced by the overload after which the behaviour returned to that for the baseline fatigue response. While the peak crack-tip stress is supressed by the compressive residual stress, the crack-tip stress field changes over each cycle are nevertheless the same for all Kmax cycles except at OL.

Authors and Affiliations

P. Withers, M. Mostafavi, A. Steuwer, J. Kelleher, T. Buslaps

Keywords

Related Articles

Fatigue life estimation in welded joints under multiaxial loadings 

Welded joints are frequently locations for cracks initiation and propagation that may cause fatigue failure of engineering structures. Biaxial or triaxial stress-strain states are present in the vicinity of welded joint...

 Investigation about crack propagation paths in thin rim gears

 Crack propagation in gears is a problem related not only to the life of the components, but also to the concept of failsafe design. Fail safe design means to design a component in order that, if a failure occurs,...

 Mechanism of crack branching in the fatigue crack growth path of 2324-T39 Aluminium alloy

 The crack growth behavior in 2324-T39 aluminium alloy was experimentally investigated. Two types of crack branching were observed. The mechanism of an uncommon crack branching which results from the link up o...

 Role of the microstructure on the mechanical properties of fully pearlitic eutectoid steels

 This paper analyses how the microstructure of an eutectoid pearlitic steel affects its conventional mechanical properties (obtained by means of a standard tension test) and the associated micromechanisms of fract...

 Effect of Carbon and Nitrogen Content on Deformation and Fracture of AISI 304 Austenitic Stainless Steel

 The effect of small differences in the content of carbon and nitrogen on the room temperature tensile deformation and fracture behaviour of an AISI 304 stainless steel was studied. In the steel containing the lower...

Download PDF file
  • EP ID EP116903
  • DOI 10.3221/IGF-ESIS.33.19
  • Views 72
  • Downloads 0

How To Cite

P. Withers, M. Mostafavi, A. Steuwer, J. Kelleher, T. Buslaps (2015).  2D mapping of plane stress crack-tip fields following an overload. Frattura ed Integrità Strutturale, 9(33), 151-158. https://europub.co.uk/articles/-A-116903