Duplex S-N fatigue curves: statistical distribution of the transition fatigue life
Journal Title: Frattura ed Integrità Strutturale - Year 2014, Vol 8, Issue 30
Abstract
In recent years, very-high-cycle fatigue (VHCF) behavior of metallic materials has become a major point of interest for researchers and industries. The needs of specific industrial fields (aerospace, mechanical and energy industry) for structural components with increasingly large fatigue lives, up to 1010 cycles (gigacycle fatigue), requested for a more detailed investigation on the experimental properties of materials in the VHCF regime. Gigacycle fatigue tests are commonly performed using resonance fatigue testing machines with a loading frequency of 20 kHz (ultrasonic tests). Experimental results showed that failure is due to cracks which nucleate at the specimen surface if the stress amplitude is above the conventional fatigue limit (surface nucleation) and that failure is generally due to cracks which nucleate from inclusions or internal defects (internal nucleation) when specimens are subjected to stress amplitudes below the conventional fatigue limit. Following the experimental evidence, the Authors recently proposed a new statistical model for the complete description of SN curves both in the high-cycle-fatigue (HCF) and in the VHCF fatigue regions (Duplex S-N curves). The model differentiates between the two failure modes (surface and internal nucleation), according to the estimated distribution of the random transition stress (corresponding to the conventional fatigue limit). No assumption is made about the statistical distribution of the number of cycles at which the transition between surface and internal nucleation occurs (i.e., the transition fatigue life). In the present paper, the statistical distribution of the transition fatigue life is obtained, according to the statistical model proposed. The resulting distribution depends on the distance between the HCF and the VHCF regions and on the distribution of the random transition stress. The estimated distribution can be effectively used to predict, with a specified confidence level, the number of cycles for which an internal nucleation may probabilistically occur in a VHCF test and it is also informative for properly choosing the end of HCF tests in terms of number of cycles. A numerical example, based on experimental datasets taken from the literature, is provided.
Authors and Affiliations
D. Paolino, A. Tridello, H. Geng, G. Chiandussi, M. Rossetto
Keywords
Related Articles
- EP ID EP142367
- DOI -
- Views 59
- Downloads 0
Propagazione di fratture longitudinali in gasdotti caratterizzati da bassa duttilità
Il presente lavoro propone l’analisi di propagazione di una frattura fragile longitudinale di un gasdotto interrato basata sulla valutazione dell’energy release rate. Viene illustrata l’implementazione della sudd...
Infrared thermography study of the fatigue crack propagation
The work is devoted to the experimental study of heat dissipation process caused by fatigue crack propagation. To investigate a spatial and time temperature evolution at the crack tip set of experiments was carried...
On the decay of strength in Guilin red clay with cracks
In order to research the effect of cracks in red clay on shear strength through dry-wet cycle test, the experimenters used imaging software and a mathematical model to determine fractal dimension and crack ratio&n...
Stress-state dependent cohesive model for fatigue crack growth
In the cohesive framework, a stress-state dependent cohesive model, combined with an irreversible damage parameter has been used in simulation of fatigue crack growth initiation and continued growth. The model is...
A dimensional analysis approach to fatigue in quasi-brittle materials
In this study, a generalized Barenblatt and Botvina dimensional analysis approach to fatigue crack growth is proposed in order to highlight and explain the deviations from the classical power-law equations used to charac...