Fatigue strength of SS400 steel under non-proportional loading
Journal Title: Frattura ed Integrità Strutturale - Year 2016, Vol 10, Issue 38
Abstract
This study discusses fatigue properties of low carbon steel, type SS400 steel, under non-proportional loading. Multiaxial fatigue tests under proportional and non-proportional loading conditions with various stress amplitudes were carried out using a hollow cylinder specimen at room temperature. In the test, three types of stress paths were employed. They are a push-pull, a reversed torsion and a circle loading. The circle loading is a cyclic loading combined the push-pull and the reversed torsion loading in which axial and shear stress waveforms have 90 degrees phase differences. From the obtained test results, poor evaluations of failure life under non-proportional loading are indicated when the life is correlated by the equivalent strain range based on von Mises Δεeq and the non-proportional strain range ΔεNP. A modified strain parameter is presented which can evaluate the failure life in high and low strain levels under non-proportional loading
Authors and Affiliations
T. Morishita
Keywords
Related Articles
- EP ID EP118215
- DOI 10.3221/IGF-ESIS.38.39
- Views 58
- Downloads 0
Effect of fibre arrangement on the multiaxial fatigue of fibrous composites: a micromechanical computational model
Structural components made of fibre-reinforced materials are frequently used in engineering applications. Fibre-reinforced composites are multiphase materials, and complex mechanical phenomena take place at l...
Photoelastic stress analysis assisted evaluation of fracture toughness in hydrothermally aged epoxies
The present work has investigated the fracture toughness of a model DGEBA epoxy system subject to Hidro-Thermal aging. A Photoelastic Stress Analysis technique has been implemented, showing the evolution of stres...
Distribuzioni di tensione per intagli soggetti a torsione in condizioni elastiche ed elastoplastiche
Il lavoro riporta delle soluzioni analitiche in forma chiusa per le distribuzioni di tensione generate da intagli circonferenziali in componenti assialsimmetrici soggetti a torsione, in condizioni lineari elastiche ed el...
Investigation about crack propagation paths in thin rim gears
Crack propagation in gears is a problem related not only to the life of the components, but also to the concept of failsafe design. Fail safe design means to design a component in order that, if a failure occurs,...
Cf/C composites: correlation between CVI process parameters and Pyrolytic Carbon microstructure
Chemical Vapour Infiltration (CVI) technique has been long used to produce carbon/carbon composites. The Pyrolytic Carbon (Py-C) matrix infiltrated by CVI could have different microstructures, i.e. Rough Laminar...