Fracture toughness of TiAl-Cr-Nb-Mo alloys produced via centrifugal casting
Journal Title: Frattura ed Integrità Strutturale - Year 2012, Vol 6, Issue 22
Abstract
Fracture toughness of a TiAl base intermetallic alloy has been investigated at room temperature. The Ti-48Al-2.5Cr-0.5Nb-2Mo (at. %) alloy produced via centrifugal casting exhibits fine nearly lamellar microstructures, consisting mainly of fine lamellar grains, together with a very small quantity of residual β phases along lamellar colony boundaries. In order to determine the alloy fracture toughness compact tension specimens were tested and the results were compared with those available in literature.
Authors and Affiliations
A. Brotzu, F. Felli, D. Pilone
Sub-critical cohesive crack propagation with hydro-mechanical coupling and friction
Looking at the long-time behaviour of a dam, it is necessary to assume that the water can penetrate a possible crack washing away some components of the concrete. This type of corrosion reduces the tensile st...
Robust design of a polygonal shaft-hub coupling
In this work, the Taguchi method is applied for the optimal choice of design parameter values for a polygonal shaft-hub coupling. The objective is to maximize a performance function, minimizing, at the same time,...
Crack initiation and propagation on the polymeric material ABS (Acrylonitrile Butadiene Styrene), under ultrasonic fatigue testing
Crack initiation and propagation have been investigated on the polymeric material ABS (Acrylonitrile Butadiene Styrene), under ultrasonic fatigue testing. Three controlled actions were implemented in order to...
Multi-scale crack closure measurements with digital image correlation on Haynes 230
An experimental campaign was developed to study fatigue crack growth in Haynes 230, a Ni-based superalloy. The effects of crack closure were investigated with digital image correlation, by applying two different...
Simulation of accelerated strip cooling on the hot rolling mill run-out roller table
A mathematical model of the thermal state of the metal in the run-out roller table continuous wide hot strip mill. The mathematical model takes into account heat generation due to the polymorphic γ → α transforma...