Sub-critical cohesive crack propagation with hydro-mechanical coupling and friction
Journal Title: Frattura ed Integrità Strutturale - Year 2016, Vol 10, Issue 35
Abstract
Looking at the long-time behaviour of a dam, it is necessary to assume that the water can penetrate a possible crack washing away some components of the concrete. This type of corrosion reduces the tensile strength and fracture energy of the concrete compared to the same parameters measured during a short-time laboratory test. This phenomenon causes the so called sub-critical crack propagation. That is the reason why the International Commission of Large Dams recommends to neglect the tensile strength of the joint between the dam and the foundation, which is the weakest point of a gravity dam. In these conditions a shear displacement discontinuity starts growing in a point, called Fictitious Crack Tip (shortened FCT), which is still subjected to a compression stress. In order to manage this problem, in this paper the cohesive crack model is re-formulated with the focus on the shear stress component. In this context, the classical Newton-Raphson method fails to converge to an equilibrium state. Therefore the approach used is based on two stages: (a) a global one in which the FCT is moved ahead of one increment; (b) a local one in which the non-linear conditions occurring in the Fracture Process Zone are taken into account. This two-stage approach, which is known in the literature as a Large Time Increment method, is able to model three different mechanical regimes occurring during the crack propagation between a dam and the foundation rock.
Authors and Affiliations
S. Valente, A. Alberto, F. Barpi
Keywords
Related Articles
- EP ID EP133250
- DOI 10.3221/IGF-ESIS.35.35
- Views 57
- Downloads 0
Growth of long fatigue cracks under non-proportional loadings – experiment and simulation
An experimental campaign was carried out on thin-walled tubes under tension and torsion. The results from experiments are measured and compared. It is observed that cracks follow a shear-dominated growth pattern...
Creep-fatigue life evaluation of high chromium ferritic steel under non-proportional loading
T Multiaxial creep-fatigue tests under non-proportional loading conditions with various strain rates were carried out using a hollow cylinder specimen of a high chromium ferritic steel at 823K in air to discuss th...
Implementation of a damage model in a finite element program for computation of structures under dynamic loading
This work is a numerical simulation of nonlinear problems of the damage process and fracture of quasi-brittle materials especially concrete. In this study, we model the macroscopic behavior of concrete material,...
Recent developments in multi-parametric three-dimensional stress field representation in plates weakened by cracks and notches
The paper deals with the three-dimensional nature and the multi-parametric representation of the stress field ahead of cracks and notches of different shape. Finite thickness plates are considered, under different...
Evaluation of near-threshold fatigue crack propagation in Ti-6Al-4V Alloy with harmonic structure created by Mechanical Milling and Spark Plasma Sintering
Titanium alloy (Ti-6Al-4V) having a bimodal “harmonic structure”, which consists of coarsegrained structure surrounded by a network structure of fine grains, was fabricated by mechanical milling (MM) and spark pl...