Oxidation Of Cyclohexane To Cyclohexanol And Cyclohexanone Using H4[α-SiW12O40]/Zr As Catalyst
Journal Title: Molekul - Year 2016, Vol 11, Issue 1
Abstract
Synthesis and preparation of polyoxometalate H4[α-SiW12O40].nH2O with Zr as support at various weights of Zr 0.01g; 0.05 g; 0.25 g; 0.5 g; 0.75 g; 1 g and 1.25 g to form H4[α- SiW12O40]/Zr was conducted. The compounds from preparation were characterized using FTIR spectroscopy and crystallinity analysis using X-Ray diffraction. Thus H4[α- SiW12O40]/Zr was applied as catalyst for oxidation of cyclohexane to cyclohexanol and cyclohexanone. Oxidation process was studied through reaction time, hydrogen peroxide amount, temperature, and weight of catalyst. FTIR spectrum of H4[α-SiW12O40]/Zr was appeared at wavenumber 771.53-979.84 cm-1 and Zr at 486.06-1481.33 cm-1. Diffraction pattern of H4[α-SiW12O40]/Zr showed that high crystallinity was identified at 2θ 8o-10o and 28.3o. Based on FTIR spectrum and XRD powder pattern, the optimum preparation of H4[α-SiW12O40]/Zr was obtained using 0.5 g of Zr. The catalytic study of cyclohexane using H4[α-SiW12O40]/Zr at 0.5 g of Zr resulted conversion about 99.73%. Catalyst can convert cyclohexane with the highest conversion then used for further deep catalytic investigation. Optimization of oxidation process resulted optimum reaction time at 2 h, 3 mL of hydrogen peroxide amount, 80 oC of temperature, and 0.038 g of catalyst. The GCMS analysis indicated the oxidation of cyclohexane using H4[α-SiW12O40]/Zr at 0.5 g of Zr formed cyclohexanol and cyclohexanone with selectivity 18.77 and 23.57, respectively.
Authors and Affiliations
Aldes Lesbani, Menik Setyowati, Risfidian Mohadi, Dedi Rohendi
Keywords
Related Articles
- EP ID EP609543
- DOI 10.20884/1.jm.2016.11.1.194
- Views 93
- Downloads 0
SYNTHESIS OF 1,4-BIS [(1-HYDROXY-4-T-BUTYL-PHENYL) METHYL]PIPERAZINE AS ANTIOXIDANTS
A study has been conducted to synthesize 1,4-bis [(1-hydroxy-4-t-butyl-phenyl)-methyl]piperazin using phenol derivate and investigate the capability of that compound, as an antioxidant. The synthesis was carried out thro...
Landfill Leachate Degradation by TiO2-Immobilized White Cement
This report presented the characterisation of white cement and TiO2-immobilised white cement prior and after photodegradation treatment. The study was also aimed at measuring the effectiveness of catalyst that was used d...
Surface-enhanced Raman Scattering (SERS) Substrate of Colloidal Ag Nanoparticles Prepared by Laser Ablation for Ascorbic Acid Detection
Ag nanoparticles were synthesized by laser ablation using an Ag plate in distilled water. This method was performed using a laser with a wavelength of 532 nm and energy of 30 mJ for 60 min. Ag nanoparticles successfully...
GALLIC ACID: A PHENOLIC ACID AND ITS ANTIOXIDANT ACTIVITY FROM STEM BARK OF CHLOROFORM EXTRACTS OF SYZYGIUM LITORALE (BLUME) AMSHOFF (MYRTACEAE)
A phenolic acid had been isolated from chloroform soluble fractions of a methanol extract of stem bark of Syzygium litorale, Fam. Myrtaceae. The structure of the isolated compound was elucidated and established as gallic...
THE INFLUENCES OF POWER VARIATIONS ON SELECTIVITY OF SYNTHESIS REACTION OF 2’-HYDROXYCHALCONE ANALOGUE UNDER MICROWAVE IRRADIATION
Some 2’-hydroxychalcone analogues have been widely used as an intermediate to synthesize various heterocyclic compounds, such as flavanones, flavanonols, flavones, flavonols and others. The heterocyclic compounds are als...