Oxidation of the AlSi6Cu4 alloy and AlSi6Cu4-graphite particles composite at the elevated temperatures

Journal Title: Archiwum Odlewnictwa - Year 2009, Vol 9, Issue 2

Abstract

Oxidation process of AlSi6Cu4 alloy as a composite matrix and of AlSi6Cu4 / 8 vol.% graphite particles composite was investigated. Composites were prepared by stirring method for suspension obtaining and by squeeze casting of the suspension. This process was examined by testing specimens annealed during up to 1000 hours at 573 K and 673 K in air atmosphere. The average oxidation state, oxide layer thickness and hardness of examined materials were measured during the annealing time. Obtained results imply the following conclusions: composite oxidizes faster than matrix alloy at both temperatures what is confirmed by higher weight gains and thicker oxide layer. The rate of oxidation of both materials gradually slows down at both temperatures. At initial stages of annealing at 673 K the rate of oxidation of both materials is much higher than that at 573 K. With increasing time of annealing the ratio of oxidation rate at 673 K to the one at 573 K comes down. Hardness of the composite is lower than that of matrix alloy before and during annealing at both temperatures. Drop in hardness at both 573 K and 673 K is the same for matrix and composite, and after about 100 hours the hardness no longer descents.

Authors and Affiliations

Z. Konopka, S. Holecek, J. Pożar, M. Nadolski, A. Zyska

Keywords

Related Articles

Nitrogen hardening of creep-resistant G-NiCr28W alloy

In the group of creep-resistant materials, most important are heat-resistant nickel-based alloys. The G-NiCr28W alloy subject to detailed examinations was observed to have two different austenite-like phases. In the inte...

Refining processes of selected copper alloys

The analysis of the refining effectiveness of the liquid copper and selected copper alloys by various micro additions and special refining substances – was performed. Examinations of an influence of purifying, modifying...

Effect of ring notch radius on the decohesion mode in AlSi alloys

The article discusses the effect of the, determined by tensile test, non-linear characteristics of AlSi alloys on the value of the shape factor k for the three different sizes of the radius of the ring notch made on roun...

The geometrical precision of the silicone matrices to the manufacturing of the models of the gear

The article presents the researches of geometrical precision of silicone casting form manufactured with using of the process of rapid prototyping of the tools (RT – Rapid Tooling). The testing casting form is applied to...

Verification of Modification Effect on Prototype Castings from GJV Using Ultrasound Checking

Reason for and risks of using of cast iron with vermicular graphite for typical construction parts. Ultrasound checking of graphite shape. Factors influencing plausibility of result. Difference between laboratory and ope...

Download PDF file
  • EP ID EP70462
  • DOI -
  • Views 146
  • Downloads 0

How To Cite

Z. Konopka, S. Holecek, J. Pożar, M. Nadolski, A. Zyska (2009). Oxidation of the AlSi6Cu4 alloy and AlSi6Cu4-graphite particles composite at the elevated temperatures. Archiwum Odlewnictwa, 9(2), 61-64. https://europub.co.uk/articles/-A-70462