Research on the Production of Sintered Powder 316
Journal Title: Analele Universitatii "Dunarea de Jos" din Galati. Fascicula IX, Metalurgie si Stiinta Materialelor - Year 2012, Vol 35, Issue 4
Abstract
The 316 austenitic stainless steel powders are typically used in applications requiring good corrosion resistance, mechanical strength at high and very low temperatures, good ductility, wear resistance, associated in some cases with adequate porosity. The paper presents some experimental research on the production of sintered 316 stainless steel powders and their characterization in terms of microstructure and wear resistance.
Authors and Affiliations
Simona BOICIUC, Florentina POTECAȘU
Keywords
Related Articles
- EP ID EP608945
- DOI -
- Views 56
- Downloads 0
Influence pressure and size particle to extraction by CO2
Supercritical fluid extraction (SFE) is an efficient extraction technique for the separation of various organic compounds from herbs, or more generally, from plant materials. These proporties of SFE make the products mor...
Half-Finished Technology of Steels and Fatigue Strength
The paper presents the bending fatigue testing for four steel brands. The test showed that the fatigue strength is decreasing with the increasing of both ingot size and the rolled sheet thickness. The fatigue strength is...
Behaviour at Nitriding in Fluidized Layer of Austenitic Stainless Steels at the Temperature of 450 °C
Stainless austenitic steels have a good corrosion resistance but reduced abrasion strength due to low strength below 200HV5. By nitriding one may ensure the obtaining of a superficial layer with increased strength that s...
Structure Effects over Behavior of Graphite Gray Iron in Running
The work aims at emphasizing the structure changes of graphite gray iron, as a result of make-casting conditions and their effects over behavior in running of several cast items. Researches consisted of complex character...
Severe Plastic Deformed Pure Aluminum by Equal Channel Angular Pressing
Samples of an aluminum alloy were subjected to an equal channel angular pressing (ECAP) at room temperature for one pass. For the several specimens severe plastic deformation process was interrupted to observe the mater...