Shear Bond Strength of Porcelain to a Base-Metal Compared to Zirconia Core
Journal Title: Journal of Dental Biomaterials - Year 2017, Vol 4, Issue 1
Abstract
ABSTRACT Statement of Problem: Recent clinical results for Zirconia all-ceramic restorations have revealed that the fracture rate 6-15% of the Zirconia framework is so low and the core of Zirconia has high stability. However, chipping-off fractures of porcelain are the most common reason for failures of Zirconia in the fixed partial dentures. Objectives: The purpose of this study was to compare the shear bond strength (SBS) of porcelain in the porcelain fused to metal and all-ceramic crowns with Zirconia core. Materials and Methods: Two groups were selected: porcelain fused to metal (PFM) and porcelain fused to Zirconia (PFZ) (n = 30).In the PFM group, a wax model (10 × 10 × 10mm)was used to cast metal base (Ni_Cr alloy). In the PFZ group, an acrylic cubic model (10 × 10 × 10mm) was made as Zirconia model for scanning.15 cubic Zirconia samples were milled by CAD-CAM. The procedure of porcelain veneering was conducted by the conventional layering technique up to 2 mm thickness (2.5 × 2.5 × 2 mm). All specimens were stored in water for 48 hrs. Thermal cycling was conducted for 20000 cycles between 55°C and 5ºC alternatively for 30s.All samples were mounted in acrylic resin and the SBS test was performed, using a universal testing machine. The analysis of data was performed at a significance level of 0.05 using Kolmogorov-Smirnov and Mann-Whitney U-test. Results: Mean of SBS in PFM and PFZ was 24.57 and 20.88, respectively. The results of Mann-Whitney test showed that there was no statistically significant difference between the two groups of porcelain fused to metal and Zirconia in item shear bond strength (p = 0.455). Conclusions: There was no significant difference between the two groups of PFM and PFZ in the item SBS.
Authors and Affiliations
SM Abrisham, A Fallah Tafti, S Kheirkhah, MA Tavakkoli
Keywords
Related Articles
- EP ID EP246225
- DOI -
- Views 59
- Downloads 0
Introducing a Dental Caries Marking Software and Evaluate Radiologists’ Disagreement in Caries Detection Using this Software
Statement of Problem: Bitewing radiograph is the main reference for diagnosis of proximal and recurrent caries. There is no software for gathering and analyzing radiologists’ opinion in the field of caries detection on d...
The Effect of Time Intervals on Heat Transfer to the Implant-Bone Interface during Preparation of a Titanium Abutment: An in Vitro Study
Statement of Problem: Thermal injury during dental implant placement and restoration is a clinical concern as it may cause bone damage and compromise osseointegration. The threshold level for heat-induced cortical bone n...
Wear Resistance of Acrylic Resin Teeth against Porcelain and Natural Teeth
Statement of Problem: The effect of porcelain surface on the antagonist acrylic teeth has not been widely studied. Objectives: This study aimed to investigate the effect of polished porcelain, glazed porcelain, and natur...
Combination Effect of Hemostatic and Disinfecting Agents on Micro-leakage of Restorations Bonded with Different Bonding Systems
Statement of Problem: Hemostatic agents may affect the micro-leakage of different adhesive systems. Also, chlorhexidine has shown positive effects on micro-leakage. However, their interaction effect has not been reported...
Effect of Shade and Light Curing Mode on the Degree of Conversion of Silorane-Based and Methacrylate-Based Resin Composites
Statement of Problem: The degree of conversion depends on the material composition, light source properties, distance from light source, light intensity, curing time, and other factors such as shade and translucency. Obj...