Structural durability assessment of welded offshore K-nodes by different local design concepts
Journal Title: Frattura ed Integrità Strutturale - Year 2009, Vol 3, Issue 9
Abstract
The structural durability design of complex welded structures should not rely only on one single design method but should apply different methods for assuring the reliability of the assessment. In this context the application of the structural stress concept, notch stress concept and crack propagation concept are discussed through the example of K-nodes used in energetic offshore constructions like oil platforms or wind power plants, presenting the state of the art.
Authors and Affiliations
C. M. Sonsino
Keywords
Related Articles
- EP ID EP97533
- DOI 10.3221/IGF-ESIS.09.01
- Views 45
- Downloads 0
Contact between the components of a knee prosthesis: numerical and experimental study
The aim of this work is the analysis of the contact area in a knee prosthesis using two different approaches. In particular, the interface between the femoral component and the polyethylene insert has been studied...
Characterisation of crack tip fields under non-uniform fatigue loading
The paper analyses previously reported work, which uses digital image correlation to measure fatigue crack closure. As well as determining crack opening loads, the information on crack shape may be used to estimate the s...
Multi-parameter approximation of stress field in a cracked specimen using purpose-built Java applications
A quality of multi-parameter approximation of the stress and displacement fields around a crack tip in a non-brittle material test specimen is studied in the paper. The stress field approximation using Williams p...
Numerical investigation on stress corrosion cracking behavior ofdissimilar weld joints in pressurized water reactor plants
There have been incidents recently where stress corrosion cracking (SCC) observed in the dissimilarmetal weld (DMW) joints connecting the reactor pressure vessel (RPV) nozzle with the hot leg pipe. Due to thecomple...
Fracture-Safe and Fatigue-Reliable Structures
Learning from history is, by popular account, something at which human beings are not particularly good; George Bernard Shaw having stated that “we learn from history that we learn nothing from history”, while th...