STUDY OF CALCIUM PHOSPHATE (DCPD) ELECTRODEPOSITION PROCESS ON THE Mg-3Al-1Zn MAGNESIUM ALLOY SURFACE
Journal Title: Materials Engineering - Materialove inzinierstvo (MEMI) - Year 2013, Vol 20, Issue 2
Abstract
Evaluation of calcium phosphating process realized on the Mg-3Al-1Zn alloy surface after grinding was investigated by electrochemical tests supported by photodocumentation. The electrodeposition treatment was performed by electrochemical method in water solution of Ca(NO3)2.4H2O, (NH4)2HPO4 and H2O2. The formation of calcium phosphate was divided into several stages and described using light microscopy. The progress in corrosion protection of created calcium phosphate layer in 0.9% NaCl after particular electrodeposition steps was evaluated by electrochemical impedance spectroscopy. The results in the form of Nyquist plots were analyzed using equivalent circuits.
Authors and Affiliations
Filip Pastorek, Branislav Hadzima
Keywords
Related Articles
- EP ID EP103883
- DOI -
- Views 131
- Downloads 0
Improvement of the wear behaviour of highly-loaded components and tools by multi-combined surface treatment
These multi-combined surface treatments lead to a significant improvement in load-supporting capacity. Critical load values of cohesive failure measured by scratch tests are tripled when compared to the individual treatm...
THE QUALITY OF MATERIALS APPLIED FOR SLEWING BEARING RACEWAY – TECHNICAL PAPER
Selected slewing bearings and their application have been described in this article. Basic causes of the damage pitch surfaces of slewing bearings have been analyzed and examples of the damage have been presented as well...
INTERNAL FRICTION USE IN MONITORING THE DEGRADATION PROCESSES IN A MATERIAL
During the measurement of the fatigue life of material, the specimen undergoes large number of stress cycles. While the observed number of cycles before failure is considered to be the most important result (often the on...
CHOSEN PROPERTIES OF SANDWICH MATERIAL Ti-304 STAINLESS STEEL AFTER EXPLOSIVE WELDING
The work deals with evaluation of joint of stainless steel 304 SS (sheet) and commercially pure Ti both after welding explosion and followed-up annealing at 600°C/1.5h/air. The bonding line shows sinusoidal character wit...
EVALUATION OF MICROSTRUCTURAL STABILITY OF DISSIMILAR WELD JOINTS
The microstructural changes occurring in the weld joint P92/316Ti during his long-term exposure at high temperature were studied. In parallel to experiments were carried out calculations of phase equilibria for the base...