STUDY ON EXTRACTION OF CORN STRAW AND CORN CELLULOSE AND THE DEGRADATION PERFORMANCE OF REGENERATED FILM
Journal Title: Topics in Chemical & Material Engineering (TCME) - Year 2018, Vol 1, Issue 1
Abstract
In this paper, corn straw and corn cob are sifted into outer layer and inner layer, respectively. Then, the cellulose was separated by acid and alkali method, dissolved in ionic liquid AmimCl, cellulose film was regenerated in water from the solution of cellulose/AmimCl. At last, the cellulose content, degree of polymerization (DP) and the degradation were studied. This study provides a chance to prepare Functional cellulose Regenerated film using relatively cheap and large amount of corn byproduct as cellulose resources. The result showed that the content of cellulose in the outer layer of corn straw is higher than the inner layer. The cellulose content in the outer layer of corn cob is higher than that in the inner layer of corn cob; The Dp of corn straw cellulose is the highest among corn straw cellulose, corn cob cellulose and corn leaf; Corn straw regenerated film can be degraded in the soil and completely degraded in just 15 days.
Authors and Affiliations
Wang ben, Pan gaofeng, Fu qiang, Li yi, Xue daliang
Keywords
Related Articles
- EP ID EP414973
- DOI 10.26480/icnmim.01.2018.446.448
- Views 72
- Downloads 0
PREPARATION AND CHARACTERIZATION OF SIDE CHAIN EPOXY MODIFIED SILICONE OIL FOR PRECURSOR FIBER OF CARBON FIBER
In the carbon fiber production process, the oil agent is a very important part that affects the quality of the carbon fiber, and the epoxy group can improve the heat resistance of the silicone oil, so the epoxy modified...
PREPARATION AND CHARACTERIZATION OF POLYURETHANE/MELAM INE INTERPENETRATING POLYMER NETWORK FOAMS
Polyurethane (PU)/melamine formaldehyde resin (MF) interpenetrating polymer network (IPN) foams were prepared by synchronous polymerization with MF and PU as raw materials. The effects of PU content on the apparent densi...
ELECTROCHROMIC NANOCOMPOSITE FILM BASED ON MONOLACUNARY DAWSON-TYPE POLYOXOMETALATE AND TIO2 NANOWIRES
Electrochromic (EC) nanocomposite films consisting of monolacunary Dawson-type polyoxometalates (POMs) K10P2W17O61 (P2W17) and TiO2 nanowires (TiO2 NW) were fabricated by combining hydrothermal and sol-gel spin coating a...
APPLICATION PROPERTIES OF ETHYL BENZOATE: ENVIRONMENTAL-FRIENDLY DYEING CARRIER FOR POLYESTER FIBER
This paper uses ethyl benzoate emulsion as dyeing carrier to low temperature dyeing of polyester fiber, inspected the effect of benzyl benzoate on the application properties of polyester fabrics and disperse dyes. Using...
STUDY ON PREPARATION AND APPLICATION OF N-TIOACF COMPOSITE
The modification of N-doping on TiO2 and preparation method of N-TiO2/ACF composite was studied to solve the problems of application under narrow wavelength range, difficult recovery, easy loss and suspension in the wate...