Study on the functionalized graphene modified waterborne polyurethane materials
Journal Title: Proceedings of the International Conference on Advanced Materials and Systems (ICAMS) - Year 2018, Vol 1, Issue
Abstract
A new type of waterborne polyurethane (WPG) is fabricated using the functionalized graphene. The mechanical properties, wear resistance, and heat aging resistance of the modified polyurethane materials were tested. The results show that the initial thermal decomposition temperature (Td5) of polyurethane films increased from 217°C to 244°C, the mechanical property of modified polyurethane film firstly decreases and then increases with the increase of functionalized grapheme. In addition, the wear resistance of modified polyurethane film decreases following the increase of functionalized grapheme. Furthermore, the heat aging resistance is best when the content of functionalized grapheme is 0.02% (wt). The centrifugal stability test shows when the content is less than 0.04%, the products are stable.
Authors and Affiliations
Song Guo, Zhiwen Ding, Xiaoyan Pang, Wenqi Wang, Yuetao Yin, Guanqun You
Keywords
Related Articles
- EP ID EP602483
- DOI 10.24264/icams-2018.I.14
- Views 166
- Downloads 0
A survey study to detect problems on salted hides and skins
Some problems originated from raw hides/skins can not be recovered by other steps in leather processing and affect adversely quality of leather. To detect these problems, a questionnaire containing 14 questions was pre...
Study regarding the development of the functional textiles with antimicrobial properties
The antimicrobial fibres, with encapsulated antimicrobial agents, prevent the bacteria developing and maintain the body under hygienic conditions a longer time, refreshing and facilitating the skin respiration, eliminati...
Comparative study on the light fastness properties of different white tanning agents
The main causes of leather goods damage is fading as well as the damages caused by sweat and body grease, mechanical deformation and ageing. Tanning agents have varied efficiency on the UV durability and stabilization of...
Study on the functionalized graphene modified waterborne polyurethane materials
A new type of waterborne polyurethane (WPG) is fabricated using the functionalized graphene. The mechanical properties, wear resistance, and heat aging resistance of the modified polyurethane materials were tested. The r...
Physical and chemical assessment of a patrimony sample
The objective of this paper was to investigate the physical and chemical properties of a sample from a national heritage private collection from the beginning of the 20th century. The fibrous composition was determined b...