Synthesis and photocatalytic application of α-Fe2O3/ZnO fine particles prepared by two-step chemical method
Journal Title: Carbon - Science and Technology - Year 2013, Vol 5, Issue 2
Abstract
Composite iron oxide-Zinc oxide (α-Fe2O3/ZnO) was synthesized by two-step method: in the first one step uniform α-Fe2O3 particles were prepared through a hydrolysis process of ferric chloride at 80 °C. In the second step, the ZnO particles were included in the α-Fe2O3 particles by a zinc acetate [Zn(Ac)2·2H2O] assisted hydrothermal method at low temperature (90 °C±C). The α-Fe2O3 and ZnO phases were identified by XRD, energy dispersive X-ray analysis (EDX). The photoreactivities of α-Fe2O3/ZnO nanoparticles under UV irradiation were quantified by the degradation of formaldehyde.
Authors and Affiliations
Patij Shah, K. S. Siddhapara, D. V. Shah, Jigar Pandya
Keywords
Related Articles
- EP ID EP49900
- DOI -
- Views 261
- Downloads 0
The effect of PTSA on preparation of mesophase carbon spheres
Mesophase spheres have been synthesized by heat-treating a medium coal tar pitch at 420 ºC for 2 hours in the presence of P-toluene sulphonic acid (PTSA). The effect of PTSA on synthesis of mesophase spheres had been stu...
Eco-friendly synthesis of Graphene using the aqueous extract of Amaranthus dubius
An eco-friendly process of reduction of graphene oxide using aqueous extract of Amaranthus dubius under refluxing method is herein reported. The colour change of the graphene oxide (GO) solution from brown to black was n...
Effect of heat treatment on MnxZn(1-x)Fe2O4 nanoparticles prepared by mechanochemical method using metal oxides
Nanoparticles of MnxZn(1-x)Fe2O4 where x = 0.625, 0.65 and 0.675 with grain size ranging between 15 nm – 25 nm were prepared by novel technique employing low temperature autocombustion. XRD, IR and TEM techniques were us...
Phase evolution of matrix of C/SiCN composite during creep testing at 1300 C
Tensile creep behavior of carbon fiber-reinforced SiCN matrix composite (C/SiCN) was investigated at 1300 °C under vacuum and 45 MPa for 30 h. As-received and 1700 °C-heat treated samples were prepared. Phase evolution a...
Oxygen reduction activity of carbon fibers cathode, and application for current generation from the NAD+ and NADH recycling reaction
Carbon fibers treated at 700 oC for 10 min. were found to have O2 reduction activity when being used as a cathode. The special type of partition combined with both cationic and anionic exchange membranes was applied betw...