The comparative studies of ADI versus Hadfield cast steel wear resistance
Journal Title: Archiwum Odlewnictwa - Year 2011, Vol 11, Issue 2
Abstract
The results of comparative studies of wear resistance of ADI versus high manganese Hadfield cast steel are presented. For evaluation of wear resistance three type of ADI were chosen. Two of them were of moderate strength ADI with 800 and 1000MPa tensile strength while the third was 1400MPa tensile strength ADI. The specimens were cut from ADI test YII type casting poured and heat treated in Institute of Foundry in Krakow. The pin on disc method was used for wear resistance experiment. The specimens had a shape of 40mm long rod with diameter 6mm. The load and speed were 100N and 0,54m/s respectively. It was concluded that the wear resistance of ADI is comparable with high manganese cast steel and in case of low tensile grade ADI and is even better for high strength ADI than Hadfield steel.
Authors and Affiliations
P. Skoczylas, A. Krzyńska, M. Kaczorowski
Keywords
Related Articles
- EP ID EP72527
- DOI -
- Views 110
- Downloads 0
Stereology of carbide phase in modified hypereutectic chromium cast iron
In paper are presented results of studies of carbide phase stereology modified hypereutectic wear resistance chromium cast iron which contains carbon about 3,5% and chromium about 25%. Three substances were applied to th...
Identification of temperature changes dynamics in selected castings as a contribution to performance life improvement
Parameters describing boundary conditions and dynamics of temperature changes during casting cooling in foundry moulds and the successive performance, especially as regards the massive cast elements, were discussed. Cons...
Refining processes of selected copper alloys
The analysis of the refining effectiveness of the liquid copper and selected copper alloys by various micro additions and special refining substances – was performed. Examinations of an influence of purifying, modifying...
Criterion for selection the optimal physical and chemical properties of cobalt aluminate powder used in investment casting process
The aim of this work was to determine physical and chemical properties of cobalt aluminate (CoAl2O4) modifiers produced by different companies and the influence of different types of modifiers on the grain size of high t...
Structure and properties of gray iron casted in the electromagnetic field
In the national [1] and foreign [2] literature the methods of improving the homogeneity of the structure of castings using forced convection of the solidifying metal in the casting mould or the crystallizer are presented...