THE EFFECT OF WEAR DEBRIS REMOVAL ON THE FRETTING OF ROUGH SURFACES
Journal Title: Tribologia - Year 2017, Vol 274, Issue 4
Abstract
Experiments were conducted using an Optimol SRV5 ball-on-disc tribotester under dry gross slip fretting conditions. A sphere of 10 mm diameter from 100Cr6 steel of 64 HRC hardness contacted a disc made of 42CrMo4 steel of lower hardness (42 HRC). Normal load was set to 45 N, the test duration was 15 min, the number of cycles was 18000, and the frequency was 20 Hz. Tests were performed at 300C temperature, and displacement amplitude was set to 0.1 mm. Wear of the disc and ball was examined by a white light interferometer Talysurf CCI Lite. Wear particles were removed from a contact zone using blow-by with compressed air of constant pressures of 0.1, 0.3, and 0.5 MPa. Disc samples had different surface topography after polishing, vapour blasting, grinding, rough milling, and finishing milling. Due to debris removal, total wear of the analysed tribological system typically increased. Debris ejection led to a decrease in the wear of discs and an increase in the wear of balls.
Authors and Affiliations
Agnieszka LENART, Paweł PAWLUS, Andrzej DZIERWA, Sławomir WOŚ
Keywords
Related Articles
- EP ID EP238215
- DOI 10.5604/01.3001.0010.5993
- Views 55
- Downloads 0
Badanie mechaniki współdziałania stykowego ze zużyciem w układach cylindrycznych o wewnętrznym styku hertzowskim
Na podstawie metody autorskiej badania mechaniki styku w połączeniu cylindrycznym oraz kinetyki jego zużywania przy tarciu ślizgowym przeprowadzono analizę numeryczną obszaru zastosowania klasycznego wzoru Hertza dla ok...
ANALIZA WŁAŚCIWOŚCI TRIBOLOGICZNYCH WYBRANYCH KOMPOZYTÓW POLIMEROWYCH NA BAZIE PTFE WSPÓŁPRACUJĄCYCH ŚLIZGOWO Z TLENKIEM GLINU (Al2O3)
W artykule przedstawiono mikrostrukturę, właściwości mechaniczne i tribologiczne kompozytów polimerowych na osnowie politetrafluoroetylenu z myślą o zastosowaniu w węzłach tarcia urządzeń realizujących ruch posuwisto-zwr...
THE CONSIDERATION ABOUT SPREAD OF ROLLING CONTACT FATIGUE LIFE IN LIGHT OF CURRENT THEORIES
Research and maintenance practice shows that the rolling bearings are characterised by extensive spread of rolling contact fatigue life. This spread is determined by construction, technological and maintenance factors. M...
APPLICATION OF ROUGH SET THEORY TO ANALYSE THE RESULTS OF EMISSION TESTS OF METAL IONS IN HIP ENDOPROSTHESIS
The aim of the study was to evaluate the usefulness of rough set theory in the analysis of endoprosthesis wear. In the article, two main parts can be distinguished: the first describes the tribological study of hip endop...
Analiza właściwości mikromechanicznych i tribologicznych powłok nanokompozytowych nc-WC/a-C i Nc-WC/a-C:H
W publikacji zostały zaprezentowane wyniki badań mikromechanicznych oraz tribologicznych powłok nc-WC/a-C i nc-WC/a-C:H osadzonych poprzez rozpylanie magnetronowe na nieutwardzonym i utwardzonym powierzchniowo tlenem sto...