The effect of zinc dithiophosphates on the friction and wear of partially stabilised zirconia. Part II. Zinc di(n-nonylphenyl, di-n-nonylphenyl) dithiophosphates tribological behaviour
Journal Title: Tribologia - Year 2010, Vol 230, Issue 2
Abstract
Frictional and wear properties of zinc di(n-nonylphenyl)dithiophosphate (MA) and di(-di-n-nonylphenyl) dithiophosphate (DA) of n-hexadecane solution in frictional contact of ionic-ZrO2, partially stabilised by Y2O3 (PSZ) tested using a ball-disk tribometer, at 25ºC, have been studied. It was found that zinc dithiophosphates significantly reduce friction and wear. The effectiveness of friction and wear reduction increases with the increasing number of n-nonyl chains of aryl in the additive molecule and with the concentration of additive solution. The sliding speed and load have a detrimental effect on their behaviour. Results of these frictional experiments are closely related to the results of adsorption data of MA and DA on PSZ powder from hydrocarbon solutions.<br/><br/>
Authors and Affiliations
Leszek Margielewski, Renata Stanecka-Badura
Keywords
Related Articles
- EP ID EP345275
- DOI -
- Views 44
- Downloads 0
Właściwości tribologiczne warstwy AL2O3 modyfikowanej dwusiarczkiem wolframu we współpracy z tworzywem PEEK/BG
Praca poświęcona jest badaniom zużycia tribologicznego warstw Al2O3 modyfikowanych dwusiarczkiem wolframu w skojarzeniu z tworzywem PEEK/BG. Wyniki badań tribologicznych obejmują pomiary oporów ruchu (określenie współczy...
EFFECT OF COARSE-TO-FINE WC GRAIN RATIO ON MECHANICAL PROPERTIES AND ABRASIVE WEAR OF WC-8Co CEMENTED CARBIDES
This study performs a comprehensive analysis concerning the amount of fine tungsten carbide (WC) grains needed for the appropriate reinforcement of the cobalt (Co) metallic binder in WC-8Co cemented carbides. The goal is...
APPLYING SURFACE PLASMA HARDENING FOR IMPROVING THE TRIBOLOGICAL CHARACTERISTICS OF STEEL PARTS
This work presents the results of experimental studies on the application of surface plasma hardening to improve the tribological characteristics of steel marks of 40CrNi, 20Cr2Ni4A, and 34CrNi1Mn. According to the obtai...
Analiza wpływu grubości warstw składowych na deformacje i pękanie powłok wielowarstwowych Ti/TiN
W artykule analizowano wpływ wielowarstwowej budowy powłok typu ceramika/metal na zwiększenie ich odporności na pękanie i ograniczenie zużycia. Analizowano deformacje i pękanie takich powłok w oparciu o wyniki badań ind...
Stan termiczny i drgania przekładni zębatej przenośnika taśmowego jako funkcja smarowania
W opracowaniu przedstawiono wyniki eksploatacyjnych badań drgań i temperatury dwustopniowej przekładni zębatej pracującej w układzie napędowym przenośnika taśmowego. Drgania rejestrowano za pomocą przenośnego miernika d...