Thin wall ductile and austempered iron castings

Journal Title: Archiwum Odlewnictwa - Year 2010, Vol 10, Issue 3

Abstract

It has been shown that it is possible to produce thin wall castings made of ductile iron with wall thickness in the range of 1.2 to 2.9 mm (without chills, cold laps and misruns). Thin wall ductile iron castings can be lighter (380 g) than their substitutes made of aluminium alloys (580g). The kinetics of austenitising transformation was studied in unalloyed ductile iron. The advance of transformations during austenitising was monitored by measurement the fraction of martensite and also by dilatometic studies. It has been shown that in thin wall ductile iron castings austenitising at 880 oC for 20 minutes is adequate to obtain the austenite matrix at the end of the first stage of austempering heat treatment cycle.

Authors and Affiliations

E. Fraś, M. Górny

Keywords

Related Articles

Structural studies of partial meltings of casting surfaces made of cobalt alloy MAR-M509

The results of structural studies of partial meltings of casting surfaces of plates made of cobalt alloy MAR-M509 have been presented. The partial meltings were formed with argon or helium plasma beam generated in electr...

Production of Steel Casts in Two-Layer Moulds with Alkaline Binders Part 1. Backing sand with the alkaline inorganic binder RUDAL

Steel casts in Z.N. POMET were produced in moulds made of the moulding sand Floster. This sand did not have good knocking out properties, required a significant binder addition (4.5-5.0 parts by weight), and the casting...

Effect of ring notch radius on the decohesion mode in AlSi alloys

The article discusses the effect of the, determined by tensile test, non-linear characteristics of AlSi alloys on the value of the shape factor k for the three different sizes of the radius of the ring notch made on roun...

Identification of temperature changes dynamics in selected castings as a contribution to performance life improvement

Parameters describing boundary conditions and dynamics of temperature changes during casting cooling in foundry moulds and the successive performance, especially as regards the massive cast elements, were discussed. Cons...

The structure of connection of the AlSi5 – HS6-5-2 compound casting obtained by alphinising

The paper presents results of the analysis of the alphinising coat connection structure of the AlSi5 silumin – high speed steel HS6-5-2 compound casting. The alphinising coat was made in the AlSi5 silumin bath with tempe...

Download PDF file
  • EP ID EP72099
  • DOI -
  • Views 99
  • Downloads 0

How To Cite

E. Fraś, M. Górny (2010). Thin wall ductile and austempered iron castings. Archiwum Odlewnictwa, 10(3), 5-10. https://europub.co.uk/articles/-A-72099