Tribological Behavior of Cermet Coatings Deposited from Submicron WC-10Co-4Cr Powders Using HVOF Spraying
Journal Title: Materials Science-Medžiagotyra - Year 2019, Vol 25, Issue 3
Abstract
In this paper, we prepared cermet coatings deposited from submicron WC-CoCr powders using high-velocity oxygen-fuel (HVOF) spraying process. The detailed microstructures, slurry erosion and sliding wear resistance of as-sprayed coatings were investigated. The slurry erosion test was performed in a rotating disk rig facility with circulating system using distilled water and 3.5 wt.% NaCl slurries. The sliding wear properties were evaluated by a pin-on-disk tribometer under different loads. The results showed that submicron coatings exhibited higher slurry erosion resistance in distilled water slurry than that in 3.5 wt.% NaCl slurry after three tests. The slurry erosion mechanism of the coatings was characterized by scratches and pull-out of carbide particle. With increasing load (from 10 N to 50 N), the coatings showed a reduction in average friction coefficient (from 0.52 to 0.44), and an increase in mass loss (from 3.3 mg to 11.4 mg). The evolution of the sliding wear characteristics of the coatings with the increase of the load was micro-cracks, carbide particle pull-out, spallation, and massive exfoliation. The sliding wear mechanism of the coatings under different loads was primarily abrasive wear.
Authors and Affiliations
Sheng Hong, Yuping Wu, Bo Wang
Keywords
Related Articles
- EP ID EP615536
- DOI 10.5755/j01.ms.25.3.19507
- Views 48
- Downloads 0
Influence of Drying Temperature on Tensile and Bursting Strength of Bacterial Cellulose Biofilm
The article presents an experimental study of mechanical properties of cellulose biofilm produced by bacterial fermentation process. Naturally derived biomaterial has great current and potential applications therefore th...
The Effect of Nanoparticle Surface State on Trap Level Distribution of Polyimide/Aluminum Nitride-montmorillonite Nanocomposite Films
The electrical properties of polyimide (PI) nanocomposites, which are widely used in microelectronic industry and electrical engineering fields, strongly depend on the surface state of nanoparticles. To explore this depe...
Data on Evaluation of the Corrosion Inhibition Effect of L-alpha-aminoisocaproate on High Carbon Steel Corrosion in Dilute Acid Media
Corrosion inhibition performance of l-alpha-aminoisocaproate on high carbon steel in 1 M HCl solution has been studied by weight loss measurement, open circuit potential measurement, optical microscopy and ATF-FTIR spect...
Dependence of Electrical and Optical Properties of Sol-gel-derived SnO2 Thin Films on Sb-substitution
In the present work, Sb-doped SnO2 (ATO) thin films were deposited on Si substrates by spin-coating method and the influence of Sb-doping on surface roughness, structural, optical and electrical properties has been inves...
Improvement of the Hydrogen-Storage Properties of Mg by Adding a Polymer CMC via Transformation-Involving Milling
The addition of CMC (Carboxymethylcellulose, Sodium Salt) may improve the hydrogen uptake-release properties of Mg since it has a relatively low melting point and the melting of CMC during transformation-involving millin...