TRIBOLOGICAL PROPERTIES OF Al2O3 + TiO2 COATINGS MANUFACTURED BY PLASMA SPRAYING
Journal Title: Tribologia - Year 2019, Vol 283, Issue 1
Abstract
In the paper the results of tribological, microscopic, and mechanical research of Al2O3 + TiO2 coatings manufactured by plasma spraying are presented. The feeding material was a powder Al2O3 + 13 wt.% TiO2 (Metco 6221, OerlikonMetco) with grain size – 45 ± 15 μm. The cylinder substrates made from stainless steel (X5CrNi18-10) had a diameter equal to 25 mm and 2 mm of thickness. The variable spray parameters were plasma torch velocity in terms of substrate and spray distance. The morphology of obtained coatings was tested by scanning electron microscope (SEM), and the microstructure was investigated by light optical microscopy (LOM) and SEM. The results of mechanical properties examinations revealed the dependence of the microhardness and fracture toughness on the spray parameters. Tribological examinations were made in the ball-on-disc mode in technical dry friction conditions. Two loads were used, 5 N and 10 N. Based on the carried out tests, it could be concluded that a shorter spray distance and a reduction of the torch velocity allows one to achieve a more compact structure, which is characterized by good adhesion at the coating-substrate interface (in range from 11 to 14 MPa) and good wear resistance.<br/><br/>
Authors and Affiliations
Leszek ŁATKA, Aneta NIEMIEC, Monika MICHALAK, Paweł SOKOŁOWSKI
Keywords
Related Articles
- EP ID EP519225
- DOI 10.5604/01.3001.0013.1431
- Views 21
- Downloads 0
ANALYSIS OF THE TEMPERATURE VALUE IN CONTACT STEEL – SOIL MATERIAL IN RELATION TO THE TYPE OF CONSTRUCTION MATERIAL
The article presents a study of the friction temperature at the contact soil soil-material. For the tests, samples of 38GSA steel padded with El-Hard 63 electrode and Hardox 600 steel were selected. The experiment was ca...
WPŁYW STĘŻENIA CZĄSTEK MAGNETYCZNYCH NA WARTOŚCI PARAMETRÓW EKSPLOATACYJNYCH W POPRZECZNYM ŁOŻYSKU ŚLIZGOWYM SMAROWANYM FERRO-OLEJEM
W niniejszej pracy została przedstawiona analiza zmian podstawowych parametrów eksploatacyjnych poprzecznego łożyska ślizgowego w aspekcie stężenia cząstek magnetycznych w ferro-oleju będącego czynnikiem smarującym. W pi...
THE IMPACT OF SELECTED LUBRICANTS ON FRETTING WEAR DEVELOPMENT IN A FRICTION PAR AXLE–SLEEVE
Complex physicochemical phenomena occurring at the interface between associated surfaces and the impact of a large number of factors makes the development of fretting wear mechanism difficult to describe and it has not r...
ANALIZA WPŁYWU WARTOŚCI LUZU ŁOŻYSKOWEGO ORAZ SZEROKOŚCI ROWKA SMARUJĄCEGO NA CHARAKTERYSTYKI FILMU OLEJOWEGO HYDRODYNAMICZNYCH ŁOŻYSK GŁÓWNYCH WAŁU KORBOWEGO
Przedstawiono analizę wpływu szerokości rowka olejowego oraz luzu łożyskowego na charakterystykę filmu olejowego w hydrodynamicznych łożyskach poprzecznych wału korbowego. Analizę przeprowadzono w celu określenia wpływu...
Ocena możliwości ograniczenia liczby powtórzeń w badaniach trwałości zmęczeniowej