Tribological resistance of high speed steel HS 6-5-2 remelted with electric arc
Journal Title: Archiwum Odlewnictwa - Year 2009, Vol 9, Issue 3
Abstract
The intensity of tribological wear of the high speed steel HS 6-5-2 remelted with the GTAW method has been compared to the heat treatment steel in a conventional way. Moreover, the types of the wear appeared during the friction. The tribiological research, were done in the technically dry friction conditions on a testing machine of the pin-on-disc T-01M. The smallest intensity of wear was shown by the high speed steel remelted with the parameters leading to obtain the biggest speed of cooling of the molten metal. The main wear type appearing during the research, was the abrasion and adhesive wear.
Authors and Affiliations
A. Dziedzic
Keywords
Related Articles
- EP ID EP71991
- DOI -
- Views 101
- Downloads 0
The influence of conventional tempering on the tribiological resistance of the high speed steel HS 6-5-2 remelted with electric arc
The influence of the conventional tempering has been defined in the paper in two different temperatures 560 C and 600 C on the intensity of tribological wear of the high speed steel HS 6-5-2 remelted with the electric ar...
Synthesis of sequential control algorithms for pneumatic drives controlled by monostable valves
Application of the Grafpol method [1] for synthesising sequential control algorithms for pneumatic drives controlled by monostable valves is presented. The developed principles simplify the MTS method of programming prod...
The structure of connection of the AlSi5 – HS6-5-2 compound casting obtained by alphinising
The paper presents results of the analysis of the alphinising coat connection structure of the AlSi5 silumin – high speed steel HS6-5-2 compound casting. The alphinising coat was made in the AlSi5 silumin bath with tempe...
Adhesion of composite carbon/hydroxyapatite coatings on AISI 316L medical steel
In this paper are contains the results of studies concerning the problems associated with increased of hydroxyapatite (HAp) adhesion, manufactured by using Pulse Laser Deposition (PLD) method, to the austenitic steel (AI...
The influence of remelting parameters of the electric arc and conventional tempering on the tribological resistance of high speed steel HS 6-5-2
The present thesis depicts the results of the research of tribological high speed steel HS 6-5-2 remelted with the electric arc. Steel was remelted with different parameters. The amperage of electric arc was changed, the...