Wear Behaviour of Hard Cr Coatings for Cold Forming Tools Under Dry Sliding Conditions
Journal Title: Tribology in Industry - Year 2012, Vol 34, Issue 1
Abstract
Cr hard coatings are largely used in industry in metal cutting and cold forming processes; This work on quantitative way represents improvement, in terms of wear resistance, which is obtained by depositing Cr hard coating on foundation material. Wear testing is done on tribometer with block –on –disc contact geometry at sliding contact of Cr hard coated sample with steel disc. Testing was performed in conditions without lubrication at variable value of contact parameters (normal load, sliding speed). Cr hard coatings in all contact conditions show smaller values of wear rate.
Authors and Affiliations
S. Mitrović, M. Babić, D. Adamović, F. Živić
Keywords
Related Articles
- EP ID EP92635
- DOI -
- Views 100
- Downloads 0
Cassava Leaf Nanoparticles (CLNPs) as a Potential Additive to Anti-Corrosion Coatings for Oil and Gas Pipeline
Characterization of synthesized cassava leaf nanoparticles (CLNPs) was carried out using SEM/EDX and Gwyddion software, XRD and TEM for cassava leaves (CL) ball milled at 36, 48, 60 and 72 hours. The morphological study...
Biomimetics Design for Tribological Applications
Biomimetics, biomimicry and bionics are synonyms for the scientific discipline of creating new structures inspired by nature. Biomimetics systematically analyses the evolutionary processes of living organisms, their stru...
Effect of Heat Treatment on the Abrasive Wear Behavior of High Chromium Iron under Dry Sliding Condition
The effect of heat treatment on the abrasive wear behavior of high chromium cast iron (NF253AHT) under dry sliding condition has been investigated. Rectangular cross sectioned samples of the alloy were produced by sand c...
Fundamental Study on No-lubricating Friction Characteristics Due to Anisotropy of Surface Properties Applied to Differential Gear
The solid frictional characteristics of surface roughness in combination with anisotropy were systematically investigated through linear reciprocating sliding tests on planar surfaces with no lubrication. Four types of t...
Effect of Refractory Elements on Wear Intensity of the Surface Layers in the Abrasive Soil Mass
The paper presents the results of researches on tthe influence of vanadium and niobium on wear intensity of the surface layers in soil mass. The investigations were conducted in the laboratory conditions on a wearing mac...