Wpływ starzenia klimatycznego na adhezję powłok akrylowych
Journal Title: Autobusy. Technika, Eksploatacja, Systemy Transportowe - Year 2018, Vol 220, Issue 6
Abstract
Investigations were carried out of climatic ageing influence on acrylic coatings adhesion to the steel substrate. Obtained results showed that ageing factors action for two years contributed to the decrease of coatings adhesion to steel substrate. Pull-off adhesion strength (examined according to PN-EN ISO 4624:2016-05) was 8 MPa in the case of unaged coating whereas, in the case of coating aged climatically, decreased to 4,3 MPa. Evaluation of unaged coating state after pull-off test revealed adhesive break between the bond layer and the acrylic coating surface on the whole area of the stamp surface. However, in the case of the climatically aged coating, the cohesive break occurred in the primer layer on the 95% area of stamp surface and the cohesive break between the bond layer and the coating surface on the 5% area of the stamp surface.
Authors and Affiliations
Danuta Kotnarowska, Dariusz Stanisławek
Keywords
Related Articles
- EP ID EP561819
- DOI 10.24136/atest.2018.124
- Views 40
- Downloads 0
Analiza likwidacji szkody komunikacyjnej powstałej wskutek dewastacji w pojeździe marki Volkswagen CC
The article analyzes the damage caused by the devastation of a Volkswagen CC car. The valuation of the car in the Info Expert system is presented as well as the calculation of the vehicle repair using the original and us...
Współczesne wymiary bezpieczeństwa zwalczania zagrożeń i zanieczyszczeń w portach morskich
The article discusses selected issues regarding contemporary security dimensions in the aspect of combating threats and pollution in seaports. Analyzing the problems of the modern dimension of safety on sea areas, the co...
Ocena stanu sektora TSL w Polsce – lata 2004-2017
Artykuł jest próbą oceny stanu sektora TSL w Polsce w latach 2004-2017. W części teoretycznej pracy przybliżono obraz i specyfikację pojęcia sektor TSL oraz zaprezentowano pozycję Polski w Rankingu LPI – Wskaźnik Wydajno...
Niskocyklowa wytrzymałość zmęczeniowa stopów układu Al-Mg w złożonym stanie naprężenia
The samples of the examined alloys AlMg2Mn0,47Fe0,5 and AlMg6 were subjected to: the oscillating bending on the four spindle machine, the oscillating bending, the bending/torsion as well as the torsion on the fatigue mac...
Ocena parametrów ekonomicznych wpływu części alternatywnych na koszty napraw powypadkowych autobusów miejskich w Polsce
W artykule podjęto próbę zasygnalizowania problematyki oceny parametrów ekonomicznych wpływu części alternatywnych na koszty napraw autobusów miejskich w Polsce. Rozważania uzupełniono o autorskie symulacje hipotetycznyc...