ANALISIS KETAHANAN ABRASI MATERIAL OUTSOLE POLYURETHANE (PU) & NITRILE BUTADINE RUBBER (NBR) PADA SAFETY SHOES CHEETAH DI PT. X
Journal Title: SINTEK JURNAL: Jurnal Ilmiah Teknik Mesin - Year 2019, Vol 13, Issue 1
Abstract
Improved quality, strength and life time in terms of abrasion resistance on safety shoes outsole Cheetah material where the process use of some material has decreased in quality, besides due to usage factors, maintenance factors, and some of these materials also experience problems during use. This study is done to determine the abrasion resistance of each Outsole Polyurethane (PU) material and Nitrile Butadiene Rubber (NBR). Abrasion resistance test on the material method used the DIN Abrasion tester. Retrieval of data on outsole material was carried out on the outsole material with new conditions and that has been used in the field for a period of 1 year with a method of measuring abrasion resistance index and density of material. Calculation of average abrasion resistance for new Polyurethane (PU) type was 37 , 11 mm3 / year, while the average abrasion resistance for Polyurethane (PU) type that has been used for 1 year was 33.19 mm3 / year so that the difference is 3.92 mm3 / year or about 11% quality decrease of abrasion resistance. The average abrasion resistance with the new Nitrile Butadiene Rubber (NBR) type was 108.26 mm3 / year, the average abrasion resistance for Nitrile Butadiene Rubber (NBR) type with conditions already used in 1 year period was 107.44 mm3 / year so that the difference is 0.82 mm3 / year or about 1% decrease in quality decrease of abrasion resistance. Abrasion tolerance limits that have been set according to the SOP (Standard Operational Procedure) against abrasion resistance if SG ≥ 0.9 then the Abrasive Max is 150 and if SG ≤ 0.9 Then the Abrasive Max is 250.
Authors and Affiliations
Suherna Suherna
Keywords
Related Articles
- EP ID EP668640
- DOI -
- Views 280
- Downloads 0
PENGARUH BENTUK BUKAAN TERHADAP KEKUATAN DAN GETARAN BALOK
Beam is widely used for building and mechanical structure. The beam characteristics must be able to answer the problem in field. In recent years, beam was made which compromised between stiffness and weight of beam. The...
ANALISIS POTENSI REFUSE DERIVED FUEL (RDF) DARI SAMPAH PADA TEMPAT PEMBUANGAN AKHIR (TPA) DI KABUPATEN TEGAL SEBAGAI BAHAN BAKAR INCINERATOR PIROLISIS
The garbage dumping in Tegal Regency has reached 989.8 m3/day and increasing every year. The percentage of waste in Murareja landfill is dominated by plastic waste which is 40.15%. The plastic waste will be processed by...
ANALISIS KETAHANAN ABRASI MATERIAL OUTSOLE POLYURETHANE (PU) & NITRILE BUTADINE RUBBER (NBR) PADA SAFETY SHOES CHEETAH DI PT. X
Improved quality, strength and life time in terms of abrasion resistance on safety shoes outsole Cheetah material where the process use of some material has decreased in quality, besides due to usage factors, maintenance...
SINTESIS FASA ɣ-Co PADA PADUAN Co26Cr6Mo0.18N DENGAN KOMBINASI METODE HOMOGENISASI 1200 oC DAN HOT ROLLING SERTA TRANSFORMASI STRUKTUR KRISTALNYA
Co-Cr-Mo alloy is a material that widely used for bioimplant in the medical field due to its corrosion resistance and mechanical properties. Structurally, recommended Co-Cr-Mo alloys for medical applications are ɣ-Co pha...
EFEK PEMASANGAN ISOLATOR TERHADAP KONSUMSI BAHAN BAKAR LPG MESIN SANGRAI BIJI KOPI INDUSTRI KECIL
Coffee beans in Jember Regency continue to be increased in line with the expansion of new crop fields. New coffee plantations plus 9 hectares were based on data from the Jember Regency Statistics Agency from 2008. Coffee...