ANALYSIS OF FRACTURE OF THIN CERAMIC AND CARBON COATINGS BY MODELING AND INDENTATION EXPERIMENTS
Journal Title: Tribologia - Year 2011, Vol 239, Issue 5
Abstract
In article consideration about deformations and failure of coating-substrate system by plastic deformation of substrate and coatings fracture were presented. Analysis were based on FEM modelling and spherical microindentation results. Such complex analysis allow to determine critical loads and corresponding stress distribution leading to coatings fracture. Ceramic TiN and carbon a-C:H coatings deposited on X10CrNi 18-8 steel substrates were under consideration. It was found that tensile stress on the coatings surfaces, caused formation of first annular cracks, is sR = 6.5 i 2.4 GPa for TiN and a-C:H coatings respectively. SEM and TEM microscopic investigations have shown great impact of coating microstructure on trough thickness crack propagation.
Authors and Affiliations
Marcin Kot, Wiesław Rakowski, Łukasz Major, Paulina Indyka
Keywords
Related Articles
- EP ID EP270999
- DOI -
- Views 46
- Downloads 0
FATIGUE LIFE LIMITATION OF CERAMIC MATERIALS DUE TO SURFACE CRACK PROPAGATION
Some ceramic materials have been found to have the optimum combination of properties that are suitable for rolling element bearing applications (high speeds, high loads, different environments). Cracks, structure defects...
TESTING THE EFFECTIVENESS OF ANTISCUFFING FLUIDS USED DURING THE TRANSPORT OF BOTTLES ON CONVEYORS
During transport on conveyor, glass bottle surfaces are damaged on their surface of contact. Wear traces in the form of rings arise. Counteracting this process involves, in particular, the use of antiscuffing fluids. The...
THE INFLUENCE OF FRICTION FORCES ON LONGITUDINAL WAVE PROPAGATION IN A STUCK DRILL STRING IN A BOREHOLE
A mathematical model and the computer software for the analysis of dynamic processes occurring in the drilling pipes in the borehole under stuck drill string release by means of an impact mechanism (a jerking device) or...
Analiza porównawcza zjawisk towarzyszących tarciu cienkich powłok ceramicznych w ruchu obrotowym, postępowym i postępowo--zwrotnym
W pracy porównano właściwości tribologiczne w ruchu postępowym, postępowo-zwrotnym i obrotowym w styku skoncentrowanym kula/płaszczyzna. Skojarzenie tarciowe stanowiła powłoka azotku wolframu o grubości 0,5 µm nałożona n...
TECHNOLOGICAL AND TRIBOLOGICAL ASPECTS OF PRECISE MACHINING
This paper is a presentation of chosen issues concerning the optimization of technological quality of machined microproducts. Machining of thin wall aluminum objects (wall thickness below 0,1 mm and a few mm in height) a...