THE GREASE CONTENT IN COMPOSITE THERMOSETTING METAL-POLYMER
Journal Title: Tribologia - Year 2013, Vol 248, Issue 2
Abstract
This paper presents the impact of the grease additive content in the metal– –polymer composite that improves the wear characteristics of the investigated composites. The investigated composite material was based on phenol-formaldehyde resin with the addition of iron and high temperature grease varying by percentage share in composite. The results of the tribological processes, which were conducted under different conditions of load and velocity, are presented. The tests were performed without external lubrication, which are technically dry conditions. After the experiments, analysis was conducted on the influence of the friction parameters and grease content in composite on wear characteristics and temperature changes. It was found that the content of grease in the composite has a positive effect on the working of the composite steel.
Authors and Affiliations
Jolanta Drabik, Janusz T. Janecki, Zbigniew Pawelec, Marek Wolszczak
THE ANALYSIS OF THE IMPACT OF THE DESIGN PARAMETERS ON THE FRICTION TORQUE IN BALL BEARINGS
One of the many factors influencing the frictional moment in the bearings are construction parameters. These parameters include curvature ratio (the ratio of the radius of the track to the diameter of the ball) and the a...
THE EFFECT OT SELECTED FACTORS ON THE PROCESS OF WEAR UNDER OSCILLATORY MOTION
On the surface of the components cooperating under the sliding motion, complex tribological wear processes take place. It leads to the volume loss of components of the friction pair direct metal to metal contact. The amo...
Statyczny i dynamiczny nacisk wywierany przez glebę pylastą na powierzchnię roboczą lemiesza płużnego
Podczas orki pyłu ilastego zmierzono, przy dwóch prędkościach uprawy – 0,355 i 1,955 m·s-1, wartość nacisku wywieranego przez glebę w czterech miejscach powierzchni roboczej lemiesza płużnego. Pozwoliło to, w oparciu o z...
Badanie zjawiska pseudoplastyczności i tiksotropii smarów litowych z wykorzystaniem spektroskopii ATR-FTIR
Właściwości tribologiczne kompozytów kauczuku butadienowo--akrylonitrylowego zawierających nanorurki węglowe