Analysis of the Inconel 600 alloy destruction process in the surrounding of oxygen, nitrogen and hydrogen
Journal Title: Archiwum Odlewnictwa - Year 2010, Vol 10, Issue 3
Abstract
This paper presents results of research, which was targeted to define reasons of the short life of sieves made from a 0.8mm diameter wire of the INCONEL 600 alloy. It was noticed that when the sieves were used in the device for the nitrogen acid production there appeared a total loss of plastic properties of the wire. It was caused by the process of diffusion of oxygen, nitrogen and metal ions which was not stopped although the protective layer of the scale was produced. It resulted in the substantial decrease of the chromium contents (to ca 1.5%) and in oxidation of the grain boundary in the wire outer layer. The diffusion of nitrogen to the wire core caused in turn the precipitation of many Cr2N nitrides in the core.
Authors and Affiliations
M. Gajewski, J. Kasińska, R. Mola
Keywords
Related Articles
- EP ID EP72128
- DOI -
- Views 93
- Downloads 0
Determination of Weibull Analysis of the Hypereutectic Silumins Reliability in Failure Time Respect
The results of dynamic evaluation of the reliability of hypereutectic AlSi17Cu3NiMg silumin under the effect of symmetrical cyclic tensile-compressive stresses were presented. Studies were carried out on a normal-running...
Process management in foundries
This paper presents the nature of process management and the basic process analysis. A general model of process management in a foundry is showed. The essential activities of processing, systems and change management are...
The structure of Ni–enriched Al–Ni molten alloy before solidification
The structure of Ni–based molten alloy, containing 88,02w.%Ni and dopped both with Zr (0,46w.%) and B (0,02w.%) has been studied by means of X–ray diffraction method at temperature 1500 K. Structure factor and pair corre...
Model of knowledge representation about materials in the form of a relational database for CAPCAST system
This study is related with one of the components of a hybrid decision support system called CAPCAST, implemented under a research project conducted by WIMIIP AGH. It is a model of knowledge representation about materials...
Bainitic-martensitic nodular cast iron with carbides
In this paper the possibility obtaining of upper bainite, lower bainite and martensite or their mixture in nodular cast iron with carbides has been presented. Conditions have been given, when in nodular cast iron with ca...