ANALYSIS OF TRIBOLOGICAL PROPERTIES OF SELECTED PTFE-BASED POLYMER COMPOSITES IN A SLIDING INTERACTION WITH ALUMINIUM OXIDE (Al2O3)
Journal Title: Tribologia - Year 2018, Vol 280, Issue 4
Abstract
The paper presents the microstructure and mechanical and tribological properties of polymer composites based on polytetrafluoroethylene (PTFE) intended for use in friction couples where reciprocating motion is performed, e.g., in compressors or actuators. Micromechanical tests carried out using the Oliver-Pharr method showed that the PTFE composite with a 40% bronze content (T8B) had the most advantageous mechanical properties (hardness H, Young’s modulus E). In turn, tribological tests that were conducted using a ballon- disc tester in the linear (reciprocating) motion showed that the polytetrafluoroethylene composite with a mixture of 25% bronze powder and 15% graphite (T4GM) had the lowest tribological wear. The tribological properties of composite T5W with 25% graphite content were not much worse. Despite the most favourable mechanical parameters, the tribological wear of composites T8B and PTFE with glassy carbon (T3Ws) was nearly twice higher due to the absence of grease formed by a graphite filling. The results show that the use of composites containing a bronze-graphite filling improves the service life of lubricant-free friction couples that perform reciprocating motion.<br/><br/>
Authors and Affiliations
Władysław SKONECZNY, Sławomir KAPTACZ, Adrian BARYLSKI, Tomasz KMITA
Keywords
Related Articles
- EP ID EP415422
- DOI 10.5604/01.3001.0012.7550
- Views 30
- Downloads 0
DISCUSSION ABOUT FUNDAMENTAL PROBLEMS OF TRIBOLOGY. PART 12 – SYSTEMATIC OF RESEARCH ACTIVITY IN TRIBOLOGY – FROM STRATEGY TO TACTIC TRIBOLOGY RESEARCH
This paper presents an attempt at systematising the issues of tribology research according to the criterion of general cognitive tasks. The existing structure covering strategy, operational art and tactics were used for...
THE INFLUENCE OF THE TYPE OF GREASE ON THE SYNERGY OF ITS COMPOSITION WITH PTFE POWDER AND COPPER POWDER
Studies of the influence of the type of grease on the synergistic effect of its compositions with PTFE powder and of copper during the lubrication of steel sliding pairs working in mixed friction area of were presented....
Struktura geometryczna powierzchni boku zęba kół zębatych a proces zmęczeniowego zużywania powierzchniowego
W pracy rozpatrywane są parametry struktury geometrycznej powierzchni boku zębów kół zębatych, ukształtowanej w końcowej fazie procesu technologicznego oraz ich wpływ na zmęczeniową wytrzymałość powierzchniową. Badaniom...
Wpływ ukształtowania struktury geometrycznej powierzchni stali na współczynnik tarcia statycznego współpracujących materiałów polimerowych
Ze względu na stosunkowo dużą wartość współczynnika tarcia statycznego dla par polimerowo-metalowych, opory tarcia w odniesieniu do sił bezwładności odgrywają znaczącą rolę w zapotrzebowaniu mocy i stratach energii podcz...
Analiza stanu biomechanicznego w stawie biodrowym po całkowitej alloplastyce z różnymi wariantami endoprotez bezcementowych
W opracowaniu wykonano modelowanie i symulacje rozkładów naprężeń i przemieszczeń w aplikacjach z bezcementowymi endoprotezami stawu biodrowego. Analizie poddano biołożyska z panewkami o strukturze warstwowej wykonane z...