Anti-fouling behaviors of surface functionalized high density polyethylene membrane in microfiltration of bovine serum albumin protein
Journal Title: Polyolefins Journal - Year 2017, Vol 4, Issue 1
Abstract
An essential characteristic for high performance inherently hydrophobic membranes such as microporous high density polyethylene (HDPE) membranes is to have a hydrophilic surface. In this project, wet chemical functionalization as a facile and effective method was developed to give a hydrophilic property to HDPE membranes using polar functional groups. KClO3, K2Cr2O7 and KMnO4 were selected as oxidizing agents. The optimum concentrations and treatment time intervals were determined for each oxidizing agent. Water contact angle and pure water flux measurements were conducted to evaluate the surface hydrophilicity and membrane performance, respectively. The results showed that among different oxidizing agents, 1wt% K2Cr2O7 solution with 60 min immersion time had the highest impact on the pure water flux. The percentage of re-construction phenomenon was about 4.70%, 21.94% and 32.6% for the HDPE membranes treated by KClO3, K2Cr2O7 and KMnO4, respectively. In addition, the attenuated total reflectance spectra-Fourier transform infrared spectroscopy (ATR-FTIR) results confirmed the presence of hydroxyl groups (O–H peak appeared at 3418.78 cm−1) in the membrane modified by KClO3. Bovine serum albumin (BSA) filtration experiments revealed that the total fouling ratio (TFR) and irreversible fouling ratio (IFR) decreased from 88.10% and 42.60% for pristine membrane to 65%, 68% and 72% and 26.60%, 29.30% and 35% for the modified membranes treated by KClO3, K2Cr2O7 and KMnO4, respectively. The results indicated that incorporation of hydrophilic functional groups on the surface of HDPE membranes improved the fouling resistance behavior.
Authors and Affiliations
Milad Fonouni Fonouni, Reza Yegani, Sattar Anarjani, Akram Tavakoli
Keywords
Related Articles
- EP ID EP283181
- DOI 10.22063/POJ.2016.1343
- Views 147
- Downloads 0
Dissymmetric dinuclear transition metal complexes as dual site catalysts for the polymerization of ethylene
A series of dissymmetric dinuclear complexes were synthesized, as dual site catalysts in ethylene polymerization, by coupling the allylated a-diimine complexes of the metals Ti, Zr, V, Ni and Pd with the ansa-zirconocene...
Evaluation of effects of thymolphthalein on thermooxidative stability of polypropylene
The present work is aimed to find a new and efficient type of antioxidants for polypropylene. Hence, effects of 3,3-bis(4-hydroxy-2-methyl-5-propan-2-ylphenyl)-2-benzofuran-1-one, generally known as thymolphthalein, on t...
Impact, thermal and biodegradation properties of high impact polystyrene/corn starch blends processed via melt extrusion
High impact polystyrene (HIPS)/corn starch blends were prepared in presence of glycerol as a plasticizer via melt extrusion process by a twin-screw extruder. The novelty of this work is first, because of the use of pre-g...
Recent advances in the polymerization of butadiene over the last decade
The stereospecific polymerization of conjugated dienes began in 1954 with the first catalysts obtained by combining TiCl4 or TiCl3 with aluminum-alkyls, i.e. the catalytic systems previously employed for ethylene and pro...
Estimation of pyrolysis product of LDPE degradation using different process parameters in a stirred reactor
Pyrolysis of low density polyethylene (LDPE) by equilibrium fluid catalytic cracking (FCC) was studied in a stirred reactor under different process parameters. In this work, the effect of process parameters such as degra...