Compression strength parallel to grain of structural ekki wood
Journal Title: Annals of WULS, Forestry and Wood Technology; Zeszyty naukowe SGGW - Year 2016, Vol 93, Issue
Abstract
Compression strength parallel to grain of structural ekki wood. Due to its extreme natural durability, high density and strength parameters, ekki wood is a well-known structural material, appreciated in Western Europe and used, among other things, in bridge building. This work establishes the density and compression strength parallel to the grain, using large samples and two types of small samples. The obtained results will confirm the good mechanical properties of ekki wood and the possibility of classifying its compression strength into the highest class of deciduous structural wood.
Authors and Affiliations
ANNA POLICIŃSKA-SERWA, Sławomir Krzosek, Paweł Kozakiewicz
Keywords
Related Articles
- EP ID EP355935
- DOI -
- Views 66
- Downloads 0
The effect of long-time storage of PRF resin on its physical and chemical properties
The effect of long-time storage of PRF resin on its physical and chemical properties. Phenol- resorcinol-formaldehyde resin was subjected to 21-month storage and its physical and chemical properties, as well as bondline...
Decorative facing of wood composite materials
Decorative facing of wood composite materials. Chips from pine (Pinus sylvestris) branches were used as a covering material of wood composites. General synthetic adhesives were used for chips bonding, as well as the natu...
Effect of molar ratio of melamine-urea-formaldehyde adhesive resins condensed no-waste method’s on the selected properties of the polycondensates during storage time III. Formaldehyde emission
Effect of molar ratio of melamine-urea-formaldehyde adhesive resins condensed no-waste method’s on the selected properties of the polycondensates during storage time. III. Formaldehyde emission. In presented article were...
Experimental testing of a spatial furniture joint
Experimental testing of a spatial furniture joint. This article deals with experimental testing of a spatial corner joint with a non-continuous, interlocking tapered tenon with a thickness of 8 mm. This type of joint was...
The analysis of production and export main forest products in selected countries. Part II
The analysis of production and export of main forest products in selected countries (B). In this paper changes in production and export of hardboard, MDF and particle board in selected countries were analysed. It was int...