Corrosion Behaviour of Nickel Plated Low Carbon Steel in Tomato Fluid
Journal Title: Leonardo Electronic Journal of Practices and Technologies - Year 2010, Vol 9, Issue 16
Abstract
This research work investigated the corrosion resistance of nickel plated low carbon steel in tomato fluid. It simulated the effect of continuous use of the material in a tomato environment where corrosion products are left in place. Low carbon steel samples were nickel electroplated at 4V for 20, 25, 30 and 35 mins using Watts solution.The plated samples were then subjected to tomato fluid environment for for 30 days. The electrode potentials mV (SCE) were measured every day. Weight loss was determined at intervals of 5 days for the duration of the exposure period. The result showed corrosion attack on the nickel- plated steel, the severity decreasing with the increasing weight of nickel coating on substrate. The result showed that thinly plated low carbon steel generally did not have any advantage over unplated steel. The pH of the tomato solution which initially was acidic was observed to progress to neutrality after 4 days and then became alkaline at the end of the thirty days test (because of corrosion product contamination of the tomato)contributing to the reduced corrosion rates in the plated samples after 10 days. Un-plated steel was found to be unsuitable for the fabrication of tomato processing machinery without some form of surface treatment –thick nickel plating is suitable as a protective coating in this environment.
Authors and Affiliations
Oluleke OLUWOLE, Oluwadamilola OLAWALE
Keywords
Related Articles
- EP ID EP85358
- DOI -
- Views 111
- Downloads 0
Design of a Manually Operated Paper-Recycling Machine
A manually operated paper-recycling machine was designed and fabricated. This was done to enable waste paper conversion into useful product. The fabricated plant consists of six major component units that include the dis...
Sensitivity of Design Parameters on the Constant-Force Behavior of Compliant Slider Mechanisms
This paper highlights the significance of sensitivity analysis as a basis for the dynamic synthesis of compliant mechanisms. Based on the results obtained from the sensitivity analysis, four models were developed and sim...
Investigation of the Inhibitive Effect of Pyrazolo [3, 4-b] Pyridine on Corrosion of Stainless Steel in 1 M HCl Solutions
The purpose of this study to investigate the effect of pyrazolo [3-4-b] pyridine on the corrosion inhibition of stainless steel in 1.0M hydrochloric acid (HCl) by using the following methods: the weight loss method, the...
Production of Detergent from Castor Oil
This research work was carried out with the objective of extraction of oil from castor seeds and its utilization to produce a synthetic detergent. Solvent extraction method was employed in extracting the oil and the tota...
Comparative Study of Synthesis Procedures for Urea - Formaldehyde Resins (Part I)
This paper presents initial results from modifying the conventional synthesis procedure of UF resins, that is reacting urea and formaldehyde first in alkaline medium and subsequently in mild acid medium at reflux (conven...