Deformation zone size around drilled hole in DP steels
Journal Title: Materials Engineering - Materialove inzinierstvo (MEMI) - Year 2014, Vol 21, Issue 2
Abstract
In the present study, there are given results of the experimental tests primarily focused on determination of dimension of plastic strained layer near drilled hole surface. Three hot rolled low carbon steels with strength ranging 416 to 967 MPa (conventional mild steel and two micro alloyed steels) were examined in the state after annealing to eliminate residual stress and after intercritical quenching. It was found that the size of deformation zones (determined by differential interference contrast light microscopy) as well as thickness of hardened layer (determined by micro-hardness tests) can be correlated with the macro-hardness of steels, however, they are also dependent on their microstructure.
Authors and Affiliations
Gejza Rosemberg, Iveta Sinaiova, Lubos Juhar
Keywords
Related Articles
- EP ID EP158465
- DOI -
- Views 92
- Downloads 0
Fatigue life analysis of die forged railway axle manufactured from C30 steel
With respect to the manufacturing process, different parts of one structural component can have different fatigue properties. In this study, the fatigue life of a railway axle manufactured from C30 steel by die forging i...
INFLUENCE OF SHOT PEENING ON AISI 316Ti FATIGUE PROPERTIES
This paper deals with examination of fatigue properties of AISI 316Ti stainless steel before and after shot peening including analysis of residual stress relaxation during rotating bending fatigue tests (f = 50 Hz, T = 2...
INFLUENCE OF COOLING RATE DURING QUENCHING ON IMPACT TOUGHNESS OF A HOT-WORK TOOL STEEL AT AMBIENT TEMPERATURE AND AT 200 °C
Gross cracking of die-casting dies with inferior toughness sometimes occurs through too low preheating temperature and/or too slow cooling during quenching. This study aimed to clarify the influence of cooling rate on th...
MICROSTRUCTURE AND FRACTOGRAPHIC ANALYSIS OF DAMAGE REASONS OF COGWHEEL
The article provides an analysis of the damaged cogwheel, which was used as the drive wheel (pinion) in the steering gear box of the construction machine. The degradation of the cogwheel arose during the warranty period,...
FRACTURE BEHAVIOUR OF P/M Cr-V LEDEBURITIC STEEL WITH DIFFERENT SURFACE ROUGHNESS
The samples made from the Vanadis 6 PM ledeburitic tool steel were surface machined to different quality and heat treated by standard regime of the processing. Three point bending tests were carried out on processed samp...