MICROSTRUCTURE AND FRACTOGRAPHIC ANALYSIS OF DAMAGE REASONS OF COGWHEEL
Journal Title: Materials Engineering - Materialove inzinierstvo (MEMI) - Year 2012, Vol 19, Issue 2
Abstract
The article provides an analysis of the damaged cogwheel, which was used as the drive wheel (pinion) in the steering gear box of the construction machine. The degradation of the cogwheel arose during the warranty period, after seven months of using of the construction machine. The experimental analysis revealed that the cause of the degradation of the cogwheel was due to high mechanical stress in the operating conditions of construction machine.
Authors and Affiliations
Karin Kocúrová, Marián Hazlinger, Mária Štefániková
Keywords
Related Articles
- EP ID EP114185
- DOI -
- Views 69
- Downloads 0
THE ANALYSIS OF CAUSES OF LORRY PISTON COMBUSTION ENGINE DAMAGE
The article deals with analysis of causes of lorry piston combustion engine damage. For docummentation and analysis of causes was used macroscopical, microscopical and scanning electron microscopy. The analysis showed th...
INFLUENCE OF COOLING RATE DURING QUENCHING ON IMPACT TOUGHNESS OF A HOT-WORK TOOL STEEL AT AMBIENT TEMPERATURE AND AT 200 °C
Gross cracking of die-casting dies with inferior toughness sometimes occurs through too low preheating temperature and/or too slow cooling during quenching. This study aimed to clarify the influence of cooling rate on th...
The investigation of the corrosion resistance of the tension clamps Skl14
At the level crossings it is possible to find the problems with the corrosion of the parts of the fastening system. These problems are especially at the rubber level crossings and in the tunnels. As a part of the thesis...
34CrMo4 steel resistance against the SSC after controlled cooling process
The sulphide stress cracking corrosion resistance of 34CrMo4 steel after the accelerated cooling process under the Ar3 temperature was investigated. Two modes of heat treatment were applied to achieve homogeneous microst...
Microstructure and properties of cast iron after laser surface hardening
Laser surface hardening of cast iron is not trivial due to the material’s heterogeneity and coarse-grained microstructure, particularly in massive castings. Despite that, hardening of heavy moulds for automotive industry...