Effect of Different Irrigation Solutions on the Colour Stability of Three Calcium Silicate-Based Materials
Journal Title: Journal of Dental Biomaterials - Year 2017, Vol 4, Issue 2
Abstract
Statement of Problem: Previous studies have shown discoloration of mineral trioxide aggregate (MTA) in contact with root canal irrigation solutions. However, there are limited data on colour stability of other calcium silicate–based materials (CSMs). Objectives: This in vitro study aimed to evaluate the colour stability of three CSMs in contact with different irrigation solutions. Materials and Methods: Three CSMs including White MTA (wMTA) Angelus, calcium enriched mixture (CEM), and Biodentine were assessed in this study. Forty five samples of each material were mixed according to the manufactures’ instructions and then placed in silicone tubes. After 24 hours, the materials were removed from the moulds and 9 samples of each material left dry or immersed in normal saline, 5% sodium hypochlorite (NaOCL), 2% chlorhexidinegluconate (CHX), or 17%EDTA for 24 hours. Colour changes were measured with a spectrophotometer. Data were evaluated with 2-way analysis of variance, one way analysis of variance and Tukey post hoc tests. Results: The highest discoloration of all materials was observed after contact with CHX. In the MTA Angelus and CEM cement groups, significant differences were observed between CHX and NaOCl and also between these two irrigants with the other three irrigants (p < 0.05). In the Biodentine group, CHX created statistically significant discoloration compared to other irrigants (p < 0.05). Only wMTA Angelus showed a significantly higher discoloration in contact with EDTA compared to normal saline and dry condition (p < 0.05). wMTA Angelus showed a significantly higher colour change compared with CEM cement and Biodentine after contact with NaOCl, CHX, and EDTA (p < 0.05). Conclusions: The contact of wMTA, CEM cement, and Biodentine with CHX should be avoided because this leads to severe discoloration. Contact with sodium hypochlorite also leads to discoloration of wMTA and CEM cements. Among of the three tested materials, wMTA showed the highest discoloration after contact with NaOCl, CHX, and EDTA.
Authors and Affiliations
F Sobhnamayan, A Adl, S Ghanbaran
Keywords
Related Articles
- EP ID EP233537
- DOI -
- Views 100
- Downloads 0
Effect of Green Tea Extract as Antioxidant on Shear Bond Strength of Resin Composite to in-Office and Home-Bleached Enamel
Statement of Problem: Shear bond strength (SBS) of home and office bleached enamel will be compromised by immediate application of composite restoration. Antioxidant agent may overcome this problem. Objectives: This in v...
The Influence of Surface Polish and Beverages on the Roughness ofNanohybrid and Microhybrid Resin Composites
Statement of the Problem: Surface roughness is a key factor in the aesthetics of restorative dentistry as it can determine the clinical quality and success of restorative materials. The chemical process of dissolution in...
The Effect of Different Polishing Methods and Storage Media on Discoloration of Resin Composites
Statement of Problem: Accumulation of plaque and staining due to a rough surface, and penetration of colourant agents from food and beverages in to the resin composite results in an incomplete polymerization. There is a...
The Role of Home Bleaching Agent on the Fracture Toughness of Resin Composites Using Four-Point Bending Test
Statement of Problem: Resin composites are a common type of tooth coloured restorative materials. These materials are brittle and their major shortcomings are sensitivity to flaws and defects, low tensile strength, and s...
Impacted Mandibular Third Molar, Associated Pathoses, and Their Relation to Angulation and Impaction Depth: A Cone Beam CT Study
Statement of problem: prophylactic removal of the impacted lower third molar (ILTM) is controversial and accompanying pathologic conditions play an important role. Objectives: The aim of the present study is to evaluate...