Effect of Magnesium Oxide Nanoparticles on Water Glass Structure
Journal Title: Archiwum Odlewnictwa - Year 2012, Vol 12, Issue 3
Abstract
An attempt has been made to determine the effect of an addition of colloidal suspensions of the nanoparticles of magnesium oxide on the structure of water glass, which is a binder for moulding and core sands. Nanoparticles of magnesium oxide MgO in propanol and ethanol were introduced in the same mass content (5wt.%) and structural changes were determined by measurement of the FT-IR absorption spectra.
Authors and Affiliations
A. Bobrowski, M. Starowicz, B. Stypuła
Keywords
Related Articles
- EP ID EP72679
- DOI 10.2478/v10266-012-0073-2
- Views 104
- Downloads 0
The programme of estimation slags propriety
This article contains information concerning the analysis of the possibility of defining refinery qualities of slag based of the thermophysical and thermodynamical data. The isues presented deals not only with refining c...
The influence of the arc plasma treatment on the structure and microhardness 100Cr6 bearing steel
The effect of arc plasma treatment on structure and microhardness of 100Cr6 steel was investigated. Four different the current intensity has been used to remelting surface of the steel. SEM and LM microscopes have been u...
Influence of modification on the structure and morphology of fractures of silumin AlSi6Cu4
The results of modification of silumin AlSi6Cu4 with additions of AlTi5B1 and AlSr10 have been showed. It was found that the modification has favorable influence into structure and fracture morphology of tested alloy.
The influence of remelting parameters of the electric arc and conventional tempering on the tribological resistance of high speed steel HS 6-5-2
The present thesis depicts the results of the research of tribological high speed steel HS 6-5-2 remelted with the electric arc. Steel was remelted with different parameters. The amperage of electric arc was changed, the...
Predicting ADI mechanical properties
Ductile cast iron was quench-hardened with the isothermal transformation according to two alternatives. The first treatment alternative consisted in the austenitizing process at temperature t = 830, 860 i 900°C and anne...